THERMAL-STABILITY AND ITS IMPROVEMENT OF THE ALUMINA MEMBRANE TOP-LAYERS PREPARED BY SOL-GEL METHODS
THERMAL-STABILITY AND ITS IMPROVEMENT OF THE ALUMINA MEMBRANE TOP-LAYERS PREPARED BY SOL-GEL METHODS
复制标题
DOI：
10.1007/bf00588309
复制
发表时间：
1991-02-01
影响因子：
4.5
通讯作者：
BURGGRAAF, AJ
中科院分区：
文献类型：
--
作者：
LIN, YS;DEVRIES, KJ;BURGGRAAF, AJ
The thermal stability of unsupported alumina membrane top-layers was studied by determining the pore structure (mainly pore size) change of alumina gels, prepared by sol-gel methods, after sintering at different temperatures ranging from 450 to 1200-degrees-C. The average pore size of the pure alumina membranes and PVA-added membranes increased sharply after sintering at temperatures higher than 1000-degrees-C. Addition of 3% lanthanum, either by mixing lanthanum nitrate in the alumina sol or impregnating lanthanum nitrate into calcined alumina gel, followed by a second heat treatment, can considerably stabilize the pore structure of the alumina membrane top-layers. The pore diameter for the lanthanum-doped membranes was stabilized within 25 nm after sintering at 1200-degrees-C for 30 h, about one-sixth of that for the pure alumina membranes after sintering at 1200-degrees-C for 30 h. The substantial increase in the pore size for the pure alumina membranes at the sintering temperature of 1000 to 1200-degrees-C was accompanied by the phase transformation from gamma-to alpha-alumina. The addition of lanthanum can raise this phase transformation temperature by about 200-degrees-C.