Tensile and compressive behavior of Ti-based bulk metallic glass composites
Tensile and compressive behavior of Ti-based bulk metallic glass composites
复制标题
钛基大块金属玻璃复合材料的拉伸和压缩行为
DOI：
10.1007/s12613-013-0769-5
复制
发表时间：
2013-06
影响因子：
4.8
通讯作者：
Lin, Jun-pin
中科院分区：
文献类型：
--
作者：
Wang, Yong-sheng;Hao, Guo-jian;Lin, Jun-pin
研究了钛基大块非晶复合材料（BMGC）的拉伸和压缩特性。单轴拉伸时，屈服应力为1380 MPa，最大强度为1516 MPa，断裂应变为4.3%;单轴压缩时，屈服应力为1580 MPa，最大强度为4010 MPa，断裂应变为29%。复合材料在压缩下表现出线性的“加工硬化”能力;然而，在拉伸载荷下的真实工程应力-应变曲线中观察到“加工软化”行为。在不同载荷下，试样的断裂面也表现出不同的性能。
This article focuses on the tensile and compressive characteristics of a Ti-based bulk metallic glass composite (BMGC). It is found that the yield stress, maximum strength, and fracture strain are 1380 MPa, 1516 MPa, and 4.3% for uniaxial tension, but 1580 MPa, 4010 MPa, and 29% for uniaxial compression, respectively. The composite displays a linear “work hardening” capacity under compression; however, the “work softening” behavior is observed in the true engineering stress-strain curve upon tensile loading. The fracture surfaces of specimens also exhibit dissimilar properties under the different loadings.
登录
查看更多内容
影响因子：
1.6
作者：
Jiang, M. Q.;Ling, Z.;Dai, L. H.
通讯作者：
Dai, L. H.
影响因子：
9.4
作者：
Szuecs, F;Kim, CP;Johnson, WL
通讯作者：
Johnson, WL
影响因子：
2.7
作者：
Hufnagel, TC;Jiao, T;Ramesh, KT
通讯作者：
Ramesh, KT
影响因子：
8.6
作者：
Z. Zhang;G. He;J. Eckert;L. Schultz
通讯作者：
Z. Zhang;G. He;J. Eckert;L. Schultz
Ti～45Al～8Nb合金定向凝固过程中的微观组织演变
影响因子：
6.2
作者：
通讯作者：
--