The role of Cr and Si in affecting high-temperature oxidation behaviour of minor Dy doped NiAl alloys
The role of Cr and Si in affecting high-temperature oxidation behaviour of minor Dy doped NiAl alloys
复制标题
Cr和Si对少量Dy掺杂NiAl合金高温氧化行为的影响
DOI：
10.1016/j.corsci.2013.08.020
复制
发表时间：
2013-12
影响因子：
8.3
通讯作者：
Gong, Sengkai
中科院分区：
文献类型：
--
作者：
Peng, Hui;Zhang, Yanli;Zhang, Tian;Gong, Sengkai
研究了 Cr/Si 共掺杂 NiAlDy 合金在 1200 °C 下的等温和循环氧化行为。结合实验结果和第一性原理计算讨论了Cr和Si在NiAlDy合金氧化中的作用。 Cr和Si会在晶界共偏析，促进氧化初期θ-Al2O3向α-Al2O3的转变。 NiAlDyCr-3Si 合金在 100 小时等温氧化后质量增加了 ∼0.64 mg/cm2，并且由于 Si 和 Cr 之间的成对亲和力可以减轻界面 Cr 沉淀的有害影响，因此表现出显着改善的循环氧化性能。
Isothermal and cyclic oxidation behaviour of Cr/Si co-doped NiAlDy alloys were investigated at 1200 °C. The role of Cr and Si in oxidation of NiAlDy alloys was discussed by combining experimental results and first-principles calculations. Cr and Si would co-segregate at grain boundaries and promoted the transformation from θ-Al2O3to α-Al2O3at initial oxidation stage. The NiAlDyCr–3Si alloy yielded a mass gain of ∼0.64 mg/cm2after 100 h isothermal oxidation and showed much improved cyclic oxidation resistance due to the pair affinity between Si and Cr which can alleviate the deleterious effect of interfacial Cr precipitation.
登录
查看更多内容
影响因子：
2.2
作者：
B. Pint
通讯作者：
B. Pint
不同温度循环热处理等离子喷涂Al@NiCr的氧化行为
影响因子：
8.3
作者：
Lijian Gu;Binglin Zou;Xizhi Fan;Shuibing Zeng;Xiaolong Chen;Ying Wang;Xueqiang Cao
通讯作者：
Xueqiang Cao
影响因子：
8.3
作者：
B. Gleeson;W. Cheung;D. Young
通讯作者：
B. Gleeson;W. Cheung;D. Young
影响因子：
1.7
作者：
Hongbo Guo;Xiaoyang Wang;S. Gong
通讯作者：
Hongbo Guo;Xiaoyang Wang;S. Gong
影响因子：
8.3
作者：
D. Prajitno;B. Gleeson;D. Young
通讯作者：
D. Prajitno;B. Gleeson;D. Young