Ba0.5Sr0.5Co0.8Fe0.2O3-δ for Oxygen Separation Membranes
Ba0.5Sr0.5Co0.8Fe0.2O3-δ for Oxygen Separation Membranes
复制标题
氧分离膜用Ba0.5Sr0.5Co0.8Fe0.2O3-δ
DOI：
10.1149/1.3495854
复制
发表时间：
2010
影响因子：
8.6
通讯作者：
E. Ivers
中科院分区：
文献类型：
--
作者：
P. Müller;L. Dieterle;E. Müller;H. Störmer;D. Gerthsen;C. Niedrig;Simon Taufall;S. Wagner;E. Ivers
Ba0的晶体结构和化学成分。 5Sr0。 5Co0。 8Fe0。研究了在 700 C 至 1000 C 之间热处理后的 2O3-δ 块状样品和粉末。X 射线衍射 (XRD) 以及透射电子显微镜 (TEM) 与能量色散 X 射线光谱 (EDXS) 相结合，用于分析单个颗粒的特性。除了立方钙钛矿相之外，在低于 900°C 的温度下还发现了六方相和其他尚未明确识别的相。
The crystal structure and chemical composition of Ba0. 5Sr0. 5Co0. 8Fe0. 2O3-δ bulk samples and powders were studied after heat treatments between 700 C and 1000 C. X-ray diffractometry (XRD) and in addition transmission electron microscopy (TEM) combined with energy dispersive X-ray spectroscopy (EDXS) was applied to analyze the properties of individual grains. Besides the cubic perovskite phase a hexagonal phase and an additional, not yet clearly identified phase was found at temperatures below 900 C.