Orientation dependence of Li-ion diffusion kinetics in LiCoO2 thin films prepared by RF magnetron sputtering
Orientation dependence of Li-ion diffusion kinetics in LiCoO2 thin films prepared by RF magnetron sputtering
复制标题
DOI：
10.1016/j.ssi.2008.02.051
复制
发表时间：
2008-05-15
影响因子：
3.2
通讯作者：
Yamamoto, Osamu
中科院分区：
文献类型：
--
作者：
Xie, Jian;Imanishi, Nobuyuki;Yamamoto, Osamu
LiCoO2 thin films with different orientations were prepared by radio frequency (RF) magnetron sputtering. The Li-ion chemical diffusion coefficients, (D) over tilde (Li) were measured using cyclic voltammetry (CV), galvanostatic intermittent titration technique (GITT), potentiostatic intermittent titration technique (PITT), and electrochemical impedance spectroscopy (EIS). It was found that the LiCoO2 thin film orientation depends on the thickness of the film. A LiCoO2 thin film with a thickness of 0.31 pm shows a high (003) orientation and that with 1.35 mu m thickness exhibits high (104) orientation. The (104) oriented thin film exhibits a larger (D) over tilde (Li) value than that of the (003) oriented thin film. The lithium ion conductivity of LiCoO2 was measured with the help of a Li/lithium ion conducting polymer/Li1-delta CoO2/lithium ion conducting polymer/Li cell. The ionic conductivity obtained was compared with that obtained from the chemical diffusion coefficient of the thin films. The ionic conductivity estimated from the PITT results was a close comparison with that measured by the electron blocking method. (C) 2008 Elsevier B.V. All rights reserved.