Bioactive composites containing TEGDMA-functionalized calcium phosphate particles: Degree of conversion, fracture strength and ion release evaluation
Bioactive composites containing TEGDMA-functionalized calcium phosphate particles: Degree of conversion, fracture strength and ion release evaluation
复制标题
DOI：
10.1016/j.dental.2016.09.021
复制
发表时间：
2016-12-01
期刊：
影响因子：
5
通讯作者：
Braga, Roberto R.
中科院分区：
文献类型：
--
作者：
Alania, Yvette;Chiari, Marina D. S.;Braga, Roberto R.
Objective. To evaluate the strength and ion release of experimental composites containing TEGDMA-functionalized calcium phosphate particles.Methods. Seven composites containing equal parts (in mols) of BisGMA and TEGDMA and 60 vol % of fillers were manipulated. Filler phase was constituted by silanized barium glass and 0% (control), 10% or 20% (volume) of dicalcium phosphate dihydrate (DPCD) particles, either non-functionalized or functionalized with two different TEDGMA contents. DCPD particles were synthesized and characterized by X-ray diffraction (XRD), elemental analysis, surface area and dynamic light scattering. Composites were tested for degree of conversion (DC) by near-FTIR. Biaxial flexural strength (BFS) was determined after 24h and 28 days in water. Calcium and phosphate release after 7 days was assessed using inductively coupled plasma optical emission spectrometry (ICP-OES). Data were analyzed by ANOVA/Tukey test (alpha:5%).Results. XRD confirmed the crystalline structure corresponding to DCPD. Elemental analysis revealed particles with zero, 14% or 22% TEGDMA, with similar D-50 (around 19 mu m) and surface areas from 3.5 to 11.4 m(2)/g. The presence of DCPD did not reduce DC. After 24h, functionalization (both 14% and 22% TEGDMA) improved composite strength in comparison to non-functionalized DCPD, both at 10% and 20% levels. After 28 days, BFS of materials containing 10% functionalized DCPD were statistically similar to the control containing only barium glass. Among composites containing 10% DCPD, particle functionalization with 14% TEGDMA did not jeopardize ion release.Significance. At 10 vol%, the use of TEGDMA-functionalized CaP particles improved composite strength in relation to non-functionalized particles, while maintaining similar ion release levels. (C) 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.