Structure and Properties of Bi0.5Na0.5TiO3-BaTiO3 Compound Ceramics
Structure and Properties of Bi0.5Na0.5TiO3-BaTiO3 Compound Ceramics
复制标题
Bi0.5Na0.5TiO3-BaTiO3复合陶瓷的结构与性能
DOI：
10.4028/www.scientific.net/amr.411.503
复制
发表时间：
2011-11
期刊：
影响因子：
--
通讯作者：
Zengzhe Xi
中科院分区：
文献类型：
--
作者：
Xiaojuan Li;Jia Zhang;Wei Long;Zhigang Zhang;Zengzhe Xi
制备了Bi_（0.5）Na_（0.5）TiO_3-xwt % BaTiO_3复相陶瓷。通过扫描电镜和X射线衍射分析研究了不同BaTiO 3含量对结构的影响。结果表明，BaTiO_3薄膜的取向是由片状BaTiO_3模板诱导的。观察到压电（d33 = 112 pC/N）和介电性质（最大值5500）的显著改善。这种改进证明了BaTiO 3模板和晶粒取向生长的明显对准。
The Bi0.5Na0.5TiO3-xwt%BaTiO3 compound ceramics were prepared. The influence of different BaTiO3 content on structure was evaluated by scanning electron microscopy and X-ray diffraction analysis. The results show oriented is induced by plate-like BaTiO3 template. Signficant improvement of the piezoelectric (d33 = 112 pC/N) and dielectric properties ( max ≈ 5500) was observed. The improvement was attested to the apparent alignment of the BaTiO3 templates and grain oriented growth.
登录
查看更多内容
影响因子：
3.9
作者：
Wei Zhao;J. Ya;Ying Xin;E. Lie;Dan Zhao;Heping Zhou
通讯作者：
Wei Zhao;J. Ya;Ying Xin;E. Lie;Dan Zhao;Heping Zhou
影响因子：
3.9
作者：
Wei Zhao;Heping Zhou;Yongke Yan;Danian Liu
通讯作者：
Wei Zhao;Heping Zhou;Yongke Yan;Danian Liu
影响因子：
3.2
作者：
E. Sabolsky;S. Trolier-McKinstry;G. Messing
通讯作者：
E. Sabolsky;S. Trolier-McKinstry;G. Messing
影响因子：
3.9
作者：
T. Shoji;Kaori Fuse;Toshio Kimura
通讯作者：
T. Shoji;Kaori Fuse;Toshio Kimura
影响因子：
5.7
作者：
Takao Motohashi;Toshio Kimura
通讯作者：
Takao Motohashi;Toshio Kimura