The Effect of Etch Time and Debond Interval upon the Shear Bond Strength of Metallic Orthodontic Brackets
The Effect of Etch Time and Debond Interval upon the Shear Bond Strength of Metallic Orthodontic Brackets
复制标题
蚀刻时间和脱粘间隔对金属正畸托槽剪切粘结强度的影响
DOI：
--
复制
发表时间：
1996
期刊：
影响因子：
--
通讯作者：
W. Rock
中科院分区：
文献类型：
--
作者：
Muhamad Subra Bin Abdullah;W. Rock
各组正畸托槽在蚀刻15、30或60秒后附着在牙釉质上，在5、15分钟或24小时后剪切力剥离。蚀刻时间为15秒/剥离时间为5分钟的试样抗剪强度明显低于其他各组。有62%的试件在粘结后出现牙面损伤。因此，建议在粘接支架时常规进行15秒的蚀刻。如果要在5分钟内结扎支架，建议在30秒内进行蚀刻。60秒的蚀刻被认为太严重，不应该使用。
Groups of orthodontic brackets were attached to enamel after etching for 15, 30 or 60 seconds, they were debonded by shear forces after 5 or 15 minutes, or 24 hours. The 15 seconds etch/5 minutes debond time specimens had much lower shear strengths than other groups. Sixty-second specimens showed evidence of tooth surface damage after tie bonding. Fifteen seconds of etching is therefore recommended routinely for bonding brackets. If a bracket is to be ligated within 5 minutes of placement, 30 seconds etching is recommended. A 60-second etch is considered too severe and should not be used.
正畸粘合树脂和蚀刻牙釉质附件的拉伸粘合强度。
DOI：
10.1016/0889-5406(87)90416-1
发表时间：
1987
期刊：
American journal of orthodontics and dentofacial orthopedics : official publication of the American Association of Orthodontists, its constituent societies, and the American Board of Orthodontics
影响因子：
--
作者：
Bryant,S;Retief,DH;Russell,CM;Denys,FR
通讯作者：
Denys,FR
不同浓度的磷酸产生的釉质蚀刻图案的变化。
DOI：
--
发表时间：
1982
期刊：
The Journal of the Dental Association of South Africa = Die Tydskrif van die Tandheelkundige Vereniging van Suid-Afrika
影响因子：
--
作者：
Denys,FR;Retief,DH
通讯作者：
Retief,DH