Characterisation of rare earth assisted plasma carbonitrided TiNi alloys
Characterisation of rare earth assisted plasma carbonitrided TiNi alloys
复制标题
稀土辅助等离子碳氮共渗TiNi合金的表征
DOI：
10.1179/1743294412y.0000000028
复制
发表时间：
2012-09
影响因子：
2.8
通讯作者：
Mi, X. J.
中科院分区：
文献类型：
--
作者：
Feng, X.;Sui, J. H.;Cai, W.;Mi, X. J.
为了增加TiNi合金的扩散层厚度，在等离子体碳氮共渗过程中加入稀土元素La和Ce。比较了稀土辅助和非稀土辅助涂层TiNi的相组成、显微组织和磨损性能。结果表明，稀土的加入使渗层厚度从2.5 μm增加到12.5 μm。稀土辅助等离子碳氮共渗试样的重量损失较小，因此，它们表现出更好的耐磨性比试样离子碳氮共渗没有稀土援助。
In order to increase the thickness of diffusion layers on TiNi alloys, the rare earth (RE) metals La and Ce were employed in the plasma carbonitriding process. The phases, microstructures and wear behaviours of the coated TiNi with and without RE assistance were compared. Experimental results indicated the addition of RE obviously increased the thickness of diffusion layer from 2·5 to 12·5 μm. Rare earth assisted plasma carbonitrided samples had less weight loss, and thus they exhibited better wear resistance than specimens plasma carbonitrided without RE assistance.
登录
查看更多内容
影响因子：
2.8
作者：
A. Yetim;A. Alsaran;A. Çelik
通讯作者：
A. Yetim;A. Alsaran;A. Çelik
影响因子：
2.8
作者：
C. Ruset;E. Grigore
通讯作者：
C. Ruset;E. Grigore
影响因子：
2.8
作者：
Mir Ghasem Hosseini;M. Momeni;M. Faraji
通讯作者：
Mir Ghasem Hosseini;M. Momeni;M. Faraji
影响因子：
6.7
作者：
M. Okada;Makoto Souwa;T. Kasai;Y. Teraoka
通讯作者：
M. Okada;Makoto Souwa;T. Kasai;Y. Teraoka
影响因子：
8.6
作者：
G. Zorn;Racheli Adadi;R. Brener;V. Yakovlev;I. Gotman;E. Gutmanas;C. Sukenik
通讯作者：
G. Zorn;Racheli Adadi;R. Brener;V. Yakovlev;I. Gotman;E. Gutmanas;C. Sukenik