Solute trapping in Al-Cu alloys caused by a 29 Tesla super high static magnetic field
Solute trapping in Al-Cu alloys caused by a 29 Tesla super high static magnetic field
复制标题
29特斯拉超高静磁场引起的Al-Cu合金中的溶质捕获
DOI：
10.1038/s41598-018-36303-5
复制
发表时间：
2019-01
影响因子：
4.6
通讯作者：
Beaugnon Eric
中科院分区：
文献类型：
--
作者：
Zheng Tianxiang;Zhou Bangfei;Zhong Yunbo;Wang Jiang;Shuai Sansan;Ren Zhongming;Debray Francois;Beaugnon Eric
Solidification of Al-Cu alloys has been investigated using a 29 Tesla super high static magnetic field (SHSMF). The results show that, by imposing a 29 Tesla SHSMF, the size of primary phases and spacing of eutectic structure have been refined through the increase of undercooling which results from the suppression of diffusion coefficient. The diffusion coefficient of atoms in the liquid matrix decreases to be about 1.2 × 10−12m2/s. The lattice constants are reduced and high dislocation density forms in the primary phase, which induces a solute trapping effects. The spacing of (110) plane in Al2Cu is corrected to be 4.3123 Å and 4.2628 Å for Al-40wt.%Cu alloys treated without and with a SHSMF. The spacing of (111) plane in Al is corrected to be 2.3351 Å and 2.3258 Å for Al-26wt.%Cu alloys treated without and with a SHSMF. The compression yield strength has been improved by about 42% from 268 MPa to 462 MPa for Al-26wt.%Cu and 42.5% from 248 MPa to 431 MPa for Al-40wt.%Cu. The maximum elastic strain increases from about 2% to 4.3% for Al-26wt.%Cu and from 2% to 4% for Al-40wt.%Cu. It is expected that SHSMF is beneficial to process materials with high mechanical properties.
登录
查看更多内容
影响因子：
6
作者：
Xi Li;Y. Fautrelle;Z. Ren
通讯作者：
Xi Li;Y. Fautrelle;Z. Ren
影响因子：
1.2
作者：
W. Youdelis;J. Cahoon
通讯作者：
W. Youdelis;J. Cahoon
影响因子：
56.9
作者：
GAYLE, FW;GOODWAY, M
通讯作者：
GOODWAY, M
DOI：
10.2320/matertrans1960.26.1
发表时间：
1985
期刊：
Materials Transactions Jim
影响因子：
--
作者：
H. Nakajima;S. Maekawa;Y. Aoki;M. Koiwa
通讯作者：
H. Nakajima;S. Maekawa;Y. Aoki;M. Koiwa
强磁场定向凝固过程中层状共晶的形态不稳定性和排列
影响因子：
9.4
作者：
Li, Xi;Ren, Zhongming;Fautrelle, Yves;Zhang, Yudong;Esling, Claude
通讯作者：
Esling, Claude