Morphology control of hydroxyapatite through hydrothermal process
Morphology control of hydroxyapatite through hydrothermal process
复制标题
水热过程控制羟基磷灰石的形貌
DOI：
10.1016/j.jallcom.2007.03.081
复制
发表时间：
2008-06
影响因子：
6.2
通讯作者：
中科院分区：
文献类型：
--
作者：
以EDTA为螯合剂，在水热条件下成功合成了羟基磷灰石（HAP）。采用SEM和XRD对样品进行了表征。XRD结果表明，产物沿沿着c轴择优取向。SEM照片显示，温度、pH值、反应时间和EDTA/Ca摩尔比等反应参数可以很好地控制晶体的尺寸。
Hexagonal hydroxyapatite (HAP) has been successfully synthesized by using EDTA as chelate under hydrothermal condition. The as-prepared samples were characterized by SEM and XRD. The XRD result indicated that the products were preferentially oriented along c-axis. The SEM photographs showed that the size of the crystals was well controlled by the reaction parameters such as temperature, pH value, reaction time and the mole ratio of EDTA/Ca.
登录
查看更多内容
影响因子：
--
作者：
S. Dorozhkin;M. Epple
通讯作者：
S. Dorozhkin;M. Epple
影响因子：
5.2
作者：
Liu, JB;Ye, XY;Yan, H
通讯作者：
Yan, H
影响因子：
2.6
作者：
Arce, H;Montero, ML;Castaño, VM
通讯作者：
Castaño, VM
影响因子：
3.8
作者：
Chen, Haifeng;Sun, Kai;Clarkson, Brian H.
通讯作者：
Clarkson, Brian H.
影响因子：
8.6
作者：
Huigang Zhang;Qingshan Zhu;Y. Wang
通讯作者：
Huigang Zhang;Qingshan Zhu;Y. Wang