Wettability of GH4099 and MHC alloys by AgCuTi, TiZrCuTi and NiCrSiB filler metals and evaluation of diffusion-brazability
Wettability of GH4099 and MHC alloys by AgCuTi, TiZrCuTi and NiCrSiB filler metals and evaluation of diffusion-brazability
复制标题
AgCuTi、TiZrCuTi 和 NiCrSiB 填充金属对 GH4099 和 MHC 合金的润湿性以及扩散钎焊性评估
DOI：
10.1016/j.jmapro.2021.02.035
复制
发表时间：
2021-04
影响因子：
6.2
通讯作者：
Cao Rui
中科院分区：
文献类型：
--
作者：
Che Hongyan;Zheng Tianming;Wang Tiejun;Li Wei;Lin Qiaoli;Yan Yingjie;Cao Rui
In order to investigate the diffusion bonding between Ni-based GH4099 alloy and Mo-based MHC alloy, the wettability of AgCuTi, TiZrCuTi and NiCrSiB filler metals on the surface of GH4099 alloy and MHC alloy was firstly performed. The results show that three kinds of filler metals have excellent wettability on the surface of two kinds of substrates, and are the suitable interlayers for joining GH4099 and MHC alloys. Secondly, diffusion bonding tests of GH4099 and MHC alloys were carried out by Gleeble thermally simulated experiments. The microstructures of three kinds of welding joints with different interlayers were compared and analyzed. It was found that Ti element had significant effects on improving the bonding strength of MHC side. A large number of Ni-Mo intermetallic compounds can easily be formed, which led to high brittleness of the joints. The experimental results showed that NiCrSiB is the best interlayer material for joining GH4099 and MHC alloys, and the shear strength of the joints can reach 116 MPa.
登录
查看更多内容
DOI：
10.1016/j.ijrmhm.2004.10.003
发表时间：
2005-03
影响因子：
3.6
作者：
D. Liaw;R. Shiue
通讯作者：
D. Liaw;R. Shiue
影响因子：
6.2
作者：
Christopher Pöhl;D. Lang;J. Schatte;H. Leitner
通讯作者：
Christopher Pöhl;D. Lang;J. Schatte;H. Leitner
DOI：
10.1016/j.ijrmhm.2018.02.014
发表时间：
2018-06
影响因子：
3.6
作者：
M. Siller;D. Lang;J. Schatte;W. Knabl;H. Clemens;V. Maier-Kiener
通讯作者：
M. Siller;D. Lang;J. Schatte;W. Knabl;H. Clemens;V. Maier-Kiener
DOI：
10.1016/j.msea.2006.02.245
发表时间：
2007-03
影响因子：
6.4
作者：
T. Nam;Jae-hwa Lee;D. Jung;Cheol-am Yu;Yinong Liu;Yeon-wook Kim
通讯作者：
T. Nam;Jae-hwa Lee;D. Jung;Cheol-am Yu;Yinong Liu;Yeon-wook Kim
DOI：
10.1007/bf02645183
发表时间：
1991-12
期刊：
Journal of Phase Equilibria
影响因子：
--
作者：
H. Okamoto
通讯作者：
H. Okamoto