Strong Perpendicular Magnetic Anisotropy at Co(111)/α-Cr2O3(0001) Interface
Strong Perpendicular Magnetic Anisotropy at Co(111)/α-Cr2O3(0001) Interface
复制标题
Co(111)/α-Cr2O3(0001) 界面处具有强垂直磁各向异性
DOI：
10.1143/apex.5.043004
复制
发表时间：
2012
影响因子：
2.3
通讯作者：
R. Nakatani
中科院分区：
文献类型：
--
作者：
Y. Shiratsuchi;H. Oikawa;S. Kawahara;Y. Takechi;T. Fujita;R. Nakatani
研究了[Pt/Co]n/α-Cr_2O_3超晶格铁磁/反铁磁界面的垂直磁各向异性。通过改变堆积周期数，分别估算了Co/α-Cr_2O_3和Pt/Co界面对PMA的贡献。结果表明，在Co/α-Cr_2O_3界面和Pt/Co界面上均存在强烈的PMA诱导。界面磁各向异性能密度随铁磁层成分的变化支持了Co/α-Cr2 O3界面的PMA。据我们所知，这是PMA在铁磁/反铁磁界面的第一次演示。
We have investigated the perpendicular magnetic anisotropy (PMA) at the ferromagnetic/antiferromagnetic interface using [Pt/Co]n/α-Cr2O3 superlattices. By changing the number of stacking periods, the contributions of the Co/α-Cr2O3 and Pt/Co interfaces to the PMA are separately estimated. The results indicate that the strong PMA is induced at the Co/α-Cr2O3 interface as well as at the Pt/Co interface. The change in the interface magnetic anisotropy energy density with the ferromagnetic layer composition supports the PMA at the Co/α-Cr2O3 interface. To the best of our knowledge, this is the first demonstration of PMA at the ferromagnetic/antiferromagnetic interface.
影响因子：
2.1
作者：
Y. Shiratsuchi;S. Kawahara;H. Noutomi;R. Nakatani
通讯作者：
Y. Shiratsuchi;S. Kawahara;H. Noutomi;R. Nakatani
影响因子：
2.3
作者：
Shiratsuchi, Yu;Fujita, Toshiaki;Nakatani, Ryoichi
通讯作者：
Nakatani, Ryoichi
影响因子：
2.1
作者：
Y. Shiratsuchi;T. Fujita;H. Noutomi;H. Oikawa;R. Nakatani
通讯作者：
Y. Shiratsuchi;T. Fujita;H. Noutomi;H. Oikawa;R. Nakatani