Upconversion luminescence of Yb3+/Tb3+/Er3+-doped fluorosilicate glass ceramics containing SrF2 nanocrystals
Upconversion luminescence of Yb3+/Tb3+/Er3+-doped fluorosilicate glass ceramics containing SrF2 nanocrystals
复制标题
含SrF2纳米晶的Yb3/Tb3/Er3掺杂氟硅酸盐玻璃陶瓷的上转换发光
DOI：
10.1016/j.jallcom.2011.01.099
复制
发表时间：
2011-04
影响因子：
6.2
通讯作者：
Luo, Qun
中科院分区：
文献类型：
--
作者：
Qiao, Xvsheng;Fan, Xianping;Xue, Zheng;Xu, Xuanhe;Luo, Qun
制备了Yb3+/Tb3+/Er3+掺杂的含SrF2纳米晶的透明碱土氟硅酸盐玻璃陶瓷，并对其微观结构和光谱性能进行了研究。用X射线衍射仪、高分辨电子显微镜和扫描电子能谱仪证实了微晶玻璃中形成了富Yb3+/Tb3+/Er3+的纳米晶。由于Yb3+向Er3+和Tb3+的有效能量转移，以及受激发的Er3+和Tb3+的低声子辅助非辐射跃迁几率，微晶玻璃表现出强烈的上转换发光行为。通过改变Yb3+/Tb3+/Er3+的比例，可以显著提高上转换发光强度，并调节发光颜色。Er3+的上转换可以描述为从单一Yb3+到单一Er3+的顺序能量转移，而Tb3+的上转换可以描述为从双Yb3+到单一Tb3+的协同能量转移。
Yb3+/Tb3+/Er3+-doped transparent alkaline earth fluorosilicate glass ceramics containing SrF2nanocrystals were prepared and their microstructures and spectroscopic properties were investigated. The formation of SrF2nanocrystals enriched with Yb3+/Tb3+/Er3+in the glass ceramics was confirmed by XRD, HRTEM and SAED. The glass ceramics exhibited intense upconversion luminescence behaviors, owing to efficient energy transfers from Yb3+to Er3+and Tb3+and low phonon assistant non-radiative transition probabilities of excited Er3+and Tb3+. The upconversion could be enhanced significantly by increasing the annealing temperature and the luminescence color could be adjusted by varying the Yb3+/Tb3+/Er3+ratio. Upconversion of Er3+could be described as sequential energy transfer from single Yb3+to single Er3+, while upconversion of Tb3+described as cooperative energy transfer from double Yb3+to single Tb3+.
登录
查看更多内容
DOI：
10.1002/bbpc.19780820820
发表时间：
1978-08
期刊：
--
影响因子：
--
作者：
J. Heber
通讯作者：
J. Heber
DOI：
10.1002/9781119356080
发表时间：
2009-08
期刊：
--
影响因子：
--
作者：
B. He
通讯作者：
B. He
影响因子：
2.5
作者：
M. Weber;J. Lynch;D. Blackburn;D. Cronin
通讯作者：
M. Weber;J. Lynch;D. Blackburn;D. Cronin
影响因子：
4.6
作者：
A. Santana-Alonso;J. Méndez-Ramos;Á. C. Yanes;J. del-Castillo;V. D. Rodríguez
通讯作者：
A. Santana-Alonso;J. Méndez-Ramos;Á. C. Yanes;J. del-Castillo;V. D. Rodríguez
DOI：
10.1021/jp055780i
发表时间：
2006-03
期刊：
The journal of physical chemistry. B
影响因子：
--
作者：
X. Fan;Jin Wang;X. Qiao;Min-quan Wang;J. Adam;Xianghua Zhang
通讯作者：
X. Fan;Jin Wang;X. Qiao;Min-quan Wang;J. Adam;Xianghua Zhang