Molten Salt Synthesis of Acicular Ba2NaNb5O15 Seed Crystals
Molten Salt Synthesis of Acicular Ba2NaNb5O15 Seed Crystals
复制标题
熔盐合成针状 Ba2NaNb5O15 晶种
DOI：
10.1111/j.1551-2916.2005.00058.x
复制
发表时间：
2005-02
期刊：
影响因子：
--
通讯作者：
Peiling Wang
中科院分区：
文献类型：
--
作者：
Qingwei Huang;Jiong Xu;Lihui Zhu;Hui Gu;Peiling Wang
采用BaCO3、Nb2O5与NaCl熔盐反应，成功地制备了针状Ba2NaNb5O15（BNN）晶种。考察了煅烧温度、时间、氧化物与盐的质量比等因素对BNN颗粒形貌的影响。当盐与氧化物的比例为2：1时，在1200°C下反应4 h，可得到高长径比、均匀的针状晶种。
Well-developed acicular Ba2NaNb5O15 (BNN) seed crystals have been successfully prepared by the reaction between BaCO3, Nb2O5 and molten NaCl salt. The effects of the calcination temperature, time, and weight ratio of the oxide mixture to salt on the morphology of BNN particles were investigated. Uniform acicular seeds with high aspect ratio could be achieved at 1200°C for 4 h with the salt-to-oxide mixture of 2:1.
登录
查看更多内容
DOI：
10.1111/j.1151-2916.2000.tb01536.x
发表时间：
2000-09-01
影响因子：
3.9
作者：
Duran, C;Trolier-McKinstry, S;Messing, GL
通讯作者：
Messing, GL
DOI：
10.1088/0022-3735/13/12/015
发表时间：
1980-12
期刊：
Journal of Physics E: Scientific Instruments
影响因子：
--
作者：
K. Johansson;T. Palm;P. Werner
通讯作者：
K. Johansson;T. Palm;P. Werner
影响因子：
3.9
作者：
J. Oliver;R. Neurgaonkar;L. Cross
通讯作者：
J. Oliver;R. Neurgaonkar;L. Cross
影响因子：
3.9
作者：
Toshio Kimura;T. Kanazawa;Takashi Yamaguchi
通讯作者：
Toshio Kimura;T. Kanazawa;Takashi Yamaguchi
影响因子：
4.5
作者：
Y. Hayashi;Toshio Kimura;Takashi Yamaguchi
通讯作者：
Y. Hayashi;Toshio Kimura;Takashi Yamaguchi