Impact of Complex Permeability Measurements Up to Millimeter-Wave Frequency Range
Impact of Complex Permeability Measurements Up to Millimeter-Wave Frequency Range
复制标题
毫米波频率范围内复杂磁导率测量的影响
DOI：
10.1109/tmag.2020.3011971
复制
发表时间：
2021
影响因子：
2.1
通讯作者：
Sai R.
中科院分区：
文献类型：
--
作者：
Yabukami S.;Nozawa K.;Tonthat L.;Okita K.;Sai R.
开发了一种使用柔性基板的高灵敏度微带线型探头，用于连续测量高达毫米波频率范围（超过 30 GHz）的薄膜磁导率。该探头可实现宽带宽和高灵敏度磁导率测量，且不受样本大小的限制。对CoFeB薄膜（45mm×25mm，厚度0.5μm）、CoNbZr薄膜（25mm×25mm，厚度3nm）和镍铁氧体薄膜（8mm×5mm，厚度1.2μm）的复磁导率进行了优化。测量的磁导率谱和铁磁共振频率与基于 Landau-Lifshitz-Gilbert 方程和高达 67 GHz 的涡流生成的理论值非常吻合。
A highly sensitive microstrip-line-type probe using a flexible substrate was developed to measure thin-film permeability continuously up to the millimeter-wave frequency range (over 30 GHz). The probe enables broad bandwidth and highly sensitive permeability measurements without sample size limitations. The complex permeability of the CoFeB film (45 mm × 25 mm and 0.5 μm in thickness), CoNbZr film (25 mm × 25 mm and 3 nm in thickness), and nickel ferrite film (8 mm × 5 mm, and 1.2 μm in thickness) were optimized. The measured permeability spectrum and ferromagnetic resonance frequency showed good agreement with the theoretical values based on the Landau-Lifshitz-Gilbert equation and eddy current generation up to 67 GHz.
登录
查看更多内容
DOI：
10.1109/9780470546314
发表时间：
1998
期刊：
--
影响因子：
--
作者：
Albert A. Smith
通讯作者：
Albert A. Smith
DOI：
10.1063/1.1134339
发表时间：
1975
期刊：
影响因子：
--
作者：
P. Calcagno;D. Thompson
通讯作者：
D. Thompson
非晶 CoNbZr 薄膜的磁振布里渊散射
影响因子：
1.5
作者：
A. Yoshihara;K. Takanashi;M. Shimoda;Osamu Kitakami Osamu Kitakami;Yutaka Shimada Yutaka Shimada
通讯作者：
Yutaka Shimada Yutaka Shimada
DOI：
10.1109/tjmj.1991.4565292
发表时间：
1991
期刊：
IEEE Translation Journal on Magnetics in Japan
影响因子：
--
作者：
Y. Shimada;J. Numazawa;Y. Yoneda;A. Hosono
通讯作者：
A. Hosono