Polyelectrolyte Multilayer Nanocoating Dramatically Reduces Bacterial Adhesion to Polyester Fabric.
Polyelectrolyte Multilayer Nanocoating Dramatically Reduces Bacterial Adhesion to Polyester Fabric.
复制标题
DOI：
10.1021/acsbiomaterials.7b00250
复制
发表时间：
2017-08-14
影响因子：
5.8
通讯作者：
Grunlan JC
中科院分区：
文献类型：
--
作者：
Smith RJ;Moule MG;Sule P;Smith T;Cirillo JD;Grunlan JC
Bacterial adhesion to textiles is thought to contribute to odor and infection. Alternately exposing polyester fabric to aqueous solutions of poly(diallyldimethylammonium chloride) (PDDA) and poly(acrylic acid) (PAA) is shown here to create a nanocoating that dramatically reduces bacterial adhesion. Ten PDDA/PAA bilayers (BL) are 180 nm thick and only increase the weight of the polyester by 2.5%. The increased surface roughness and high degree of PAA ionization leads to a surface with a negative charge that causes a reduction in adhesion of Staphylococcus aureus by 50% when compared to uncoated fabric, after rinsing with sterilized water, because of electrostatic repulsion. S. aureus bacterial adhesion was quantified using bioluminescent radiance measured before and after rinsing, revealing 99% of applied bacteria were removed with a ten bilayer PDDA/PAA nanocoating. The ease of processing, and benign nature of the polymers used, should make this technology useful for rendering textiles antifouling on an industrial scale.
登录
查看更多内容
影响因子：
3.9
作者：
Elzbieciak, M.;Zapotoczny, S.;Warszynski, P.
通讯作者：
Warszynski, P.
影响因子：
3.9
作者：
Holder, Kevin M.;Cain, Amanda A.;Grunlan, Jaime C.
通讯作者：
Grunlan, Jaime C.
影响因子：
9.5
作者：
Humood, Mohammad;Chowdhury, Shahla;Polycarpou, Andreas A.
通讯作者：
Polycarpou, Andreas A.
混合分枝杆菌感染的实时生物发光成像。
影响因子：
3.7
作者：
Chang M;Anttonen KP;Cirillo SL;Francis KP;Cirillo JD
通讯作者：
Cirillo JD
影响因子：
5.5
作者：
Itano, K;Choi, JY;Rubner, MF
通讯作者：
Rubner, MF