Characterization of Ni-Infiltrated GDC Electrodes for Solid Oxide Cell Applications
Characterization of Ni-Infiltrated GDC Electrodes for Solid Oxide Cell Applications
复制标题
用于固体氧化物电池应用的渗镍 GDC 电极的表征
DOI：
10.1149/2.0501409jes
复制
发表时间：
2014
影响因子：
3.9
通讯作者：
Lomberg M
中科院分区：
文献类型：
--
作者：
Lomberg M
Solid Oxide Cell (SOC) electrodes have been fabricated by infiltration of a porous gadolinia-doped ceria (GDC) scaffold with nickel nano-particles. Interconnected Ni structures were achieved with a conductivity of 620S/cm at 700 C at a Ni content of only 14 wt%. Electrochemical performance in fuel cell mode was evaluated using both two-electrode symmetrical cell and three-electrode fuel cell measurements over a range of temperatures (580–750 C) and hydrogen concentrations (20–80%). At 750 C and in 50% H 2-50% N 2 the area specific resistance was as low as 0.14 Ω· cm 2. The charge transfer activation energy of hydrogen oxidation on these electrodes was∼ 0.53–0.58 eV, lower than that previously reported for conventional Ni-YSZ electrodes. The microstructure of the electrode was studied using Scanning Electron Microscopy. Formation of Ni agglomerates and increased ohmic resistance was observed over approximately 100 hrs of cell operation at 690 C and 50% H 2-50% N 2, though charge transfer resistance was little affected. The results indicate the feasibility of percolated Ni-infiltrated GDC electrodes for future application in SOCs and highlight some of their challenges.
登录
查看更多内容
使用参比电极分析 SOFC
影响因子：
3.9
作者：
H. Finklea;Xiaoke Chen;K. Gerdes;S. R. Pakalapati;I. Celik
通讯作者：
I. Celik
使用电化学阻抗谱补偿固体氧化物燃料电池电极三电极测量极化曲线时的误差
影响因子：
6.6
作者：
G. Offer;P. Shearing;J. Golbert;D. Brett;A. Atkinson;N. Brandon
通讯作者：
N. Brandon
固体氧化物燃料电池纳米晶镍/氧化钆掺杂二氧化铈薄膜阳极的电化学性能
DOI：
--
发表时间：
2008
期刊：
影响因子：
--
作者：
U. Muecke;K. Akiba;A. Infortuna;T. Šalkus;N. Stus;L. Gauckler
通讯作者：
L. Gauckler
对圆盘电极上进行的动力学测量的修正
DOI：
--
发表时间：
1989
期刊：
影响因子：
--
作者：
A. West;J. Newman
通讯作者：
J. Newman
掺杂二氧化铈与氧化锆的固相反应过程
DOI：
--
发表时间：
2000
期刊：
影响因子：
--
作者：
K. Eguchi;N. Akasaka;H. Mitsuyasu;Yasushi Nonaka
通讯作者：
Yasushi Nonaka