A novel ultrafine-grained Ni3Al with increased cyclic oxidation resistance
A novel ultrafine-grained Ni3Al with increased cyclic oxidation resistance
复制标题
一种具有增强循环氧化性能的新型超细晶 Ni3Al
DOI：
10.1016/j.corsci.2011.01.043
复制
发表时间：
2011-04
影响因子：
8.3
通讯作者：
M. Li
中科院分区：
文献类型：
--
作者：
X. Peng;M. Li
将电沉积Ni-Al复合材料在600°C下真空退火2 h制备出超细晶Ni 3Al。与电弧熔炼制备的成分相似但晶粒粗大的（CG）合金相比，UFG Ni 3Al在900°C下表现出显著提高的抗循环氧化性。微观结构的研究表明，CG合金生长的规模具有很高的敏感性屈曲和开裂，因为在规模/金属界面处形成大的空隙，但UFG合金生长的粘附规模，因为其典型的结构，防止在氧化过程中形成的界面空隙。
An ultrafine-grained (UFG) Ni3Al was fabricated by annealing an electrodeposited Ni–Al composite in vacuum at 600°C for 2h. The UFG Ni3Al, compared to a compositional-similar but coarse-grained (CG) alloy prepared by arc-melting, exhibited a greatly increased cyclic oxidation resistance at 900°C. Microstructural investigation showed that the CG alloy grew a scale with a high susceptibility to buckling and cracking because of the formation of large voids at the scale/metal interface, but that the UFG alloy grew an adherent scale, because its typical structure prevented the formation of the interface void during oxidation.
登录
查看更多内容
影响因子：
4.4
作者：
V. Haanappel;P. Pérez;J. L. González-carrasco;M. F. Stroosnijder
通讯作者：
V. Haanappel;P. Pérez;J. L. González-carrasco;M. F. Stroosnijder
影响因子：
6
作者：
Y. Zhou;X. Peng;Fu-Xin Wang
通讯作者：
Y. Zhou;X. Peng;Fu-Xin Wang
影响因子：
9.7
作者：
P. Hou
通讯作者：
P. Hou
影响因子：
9.4
作者：
R. Christensen;D. M. Lipkin;D. Clarke
通讯作者：
R. Christensen;D. M. Lipkin;D. Clarke
影响因子：
8.3
作者：
BRUMM, MW;GRABKE, HJ
通讯作者：
GRABKE, HJ