Novel low-firing microwave dielectric ceramics: BaMV2O7 (M=Mg, Zn)
Novel low-firing microwave dielectric ceramics: BaMV2O7 (M=Mg, Zn)
复制标题
新型低烧微波介质陶瓷：BaMV2O7（M=Mg、Zn）
DOI：
10.1016/j.ceramint.2014.08.032
复制
发表时间：
2014-12
影响因子：
5.2
通讯作者：
Zhang, Hui
中科院分区：
文献类型：
--
作者：
Wei, Zhenhai;Su, Congxue;Xiang, Fei;Zhang, Hui
采用传统的固体陶瓷工艺制备了新型低烧微波介质陶瓷BaMV2O7（M=Mg, Zn）。bamgv2o7和baznv2o7粉末在700℃下均可形成纯正交相。在830℃和720℃致密化温度下烧结的bamgv2o7和baznv2o7具有良好的微波介电性能：εr=8.2和10.7,Q×f=37600 GHz （11.7 GHz）和31000 GHz， τf分别= - 35.2 ppm/°C和- 64.4 ppm/°C。
Novel low-firing microwave dielectric ceramics BaMV2O7(M=Mg, Zn) were prepared by the conventional solid-state ceramic route. A pure orthorhombic phase can be formed at 700 °C for both BaMgV2O7and BaZnV2O7powders. Two promising ceramics BaMgV2O7and BaZnV2O7sintered at densification temperatures (830 °C and 720 °C, respectively) were found to possess good microwave dielectric properties:εr=8.2 and 10.7,Q×f=37600 GHz (at 11.7 GHz) and 31000 GHz, andτf=−35.2 ppm/°C and −64.4 ppm/ °C, respectively.
登录
查看更多内容
影响因子：
3.2
作者：
SHANNON, RD
通讯作者：
SHANNON, RD
影响因子：
3.9
作者：
Di Zhou;C. Randall;Hong Wang;L. Pang;X. Yao
通讯作者：
Di Zhou;C. Randall;Hong Wang;L. Pang;X. Yao
影响因子：
3.9
作者：
Song, Myung-Eun;Kim, Jin-Seong;Choi, Byung-Hyun
通讯作者：
Choi, Byung-Hyun
LiCa3ZnV3O12：一种新型低烧、高 Q 值微波介电陶瓷
影响因子：
5.2
作者：
Fang, Liang;Wei, Zhenhai;Kuang, Xiaojun;Zhang, Hui
通讯作者：
Zhang, Hui
影响因子：
5.2
作者：
J. Y. Wu;J. Bian
通讯作者：
J. Y. Wu;J. Bian