Synthesis of Ni-Al-ZrO2(Y2O3) composite coatings with excellent wear resistance through mechanical alloying combined with pulse electrodeposition
Synthesis of Ni-Al-ZrO2(Y2O3) composite coatings with excellent wear resistance through mechanical alloying combined with pulse electrodeposition
复制标题
机械合金化结合脉冲电沉积合成耐磨性能优异的Ni-Al-ZrO2(Y2O3)复合涂层
DOI：
10.1016/j.ceramint.2019.07.288
复制
发表时间：
2019-12
影响因子：
5.2
通讯作者：
Xiong Dangsheng
中科院分区：
文献类型：
--
作者：
Yan Chengqi;Li Hang;Li Jianliang;Tong Wei;Kang Yonghai;Xiong Dangsheng
采用脉冲电沉积技术对机械合金化制备的Ni-Al-ZrO2(Y2O3)涂层的粗糙表面进行堆焊。结果表明，镀镍涂层完全填充了涂层的粗糙表面。 Ni-Al金属间化合物与ZrO2(Y2O3)的结合使涂层在室温(RT)至500℃范围内表现出优异的耐磨性，广泛扩展了铝合金在工业中的应用。
Pulse electrodeposition technology was applied to pad the rough surface of Ni-Al-ZrO2(Y2O3) coating fabricated by mechanical alloying. Results indicated that the plated Ni coating padded the rough surface of the coating completely. The combination of Ni-Al intermetallics and ZrO2(Y2O3) made the coating exhibit excellent wear resistance from room temperature (RT) to 500 °C, which expanded the application of Al alloy in industry extensively.
登录
查看更多内容
影响因子：
5.2
作者：
J. G. Thakare;C. Pandey;R. S. Mulik;M. Mahapatra
通讯作者：
J. G. Thakare;C. Pandey;R. S. Mulik;M. Mahapatra
影响因子：
5.2
作者：
Chen Yan;D. Xiong;Jianliang Li
通讯作者：
Chen Yan;D. Xiong;Jianliang Li
影响因子：
6.2
作者：
Pai, Anand;Sharma, Sathya Shankar;Nikhil, R. G.
通讯作者：
Nikhil, R. G.
影响因子：
9.5
作者：
Li, Shuangjian;An, Yulong;Hou, Guoliang
通讯作者：
Hou, Guoliang
影响因子：
6.2
作者：
N. Kaushik;R. Rao
通讯作者：
N. Kaushik;R. Rao