Fabrication of an Al2O3/YAG/ZrO2 Ternary Eutectic by Combustion Synthesis Melt Casting Under Ultra-High Gravity
Fabrication of an Al2O3/YAG/ZrO2 Ternary Eutectic by Combustion Synthesis Melt Casting Under Ultra-High Gravity
复制标题
超高重力下燃烧合成熔体铸造制备Al2O3/YAG/ZrO2三元共晶
DOI：
10.1111/j.1551-2916.2008.02911.x
复制
发表时间：
2009-02
影响因子：
3.9
通讯作者：
金海波
中科院分区：
文献类型：
--
作者：
金海波
本文提出了一种制备Al2O3/YAG/ZrO2三元共晶材料的新方法，即燃烧合成熔融铸造与超高重力（UHG）技术相结合。制备产物的相对密度为理论密度的99.3%。相组成和显微组织分析表明，UHG的应用产生了无金属的陶瓷显微组织，没有孔隙和微裂纹。显微组织由分散在Al2O3中的ZrO2棒组成。产品维氏硬度为17.82 GPa，断裂韧性为5.51 MPa·m1/2。
This work presents a novel method for preparing an Al2O3/YAG/ZrO2 ternary eutectic whereby combustion synthesis melt casting has been combined with the ultra-high gravity (UHG) technique. The fabricated product had a relative density of 99.3% of the theoretical one. Phase composition and microstructure analyses indicated that the application of UHG resulted in a metal-free ceramic microstructure with no porosity or microcracks. The microstructure comprises ZrO2 rods dispersed in Al2O3. The product had 17.82 GPa Vickers hardness and 5.51 MPa·m1/2 fracture toughness.
登录
查看更多内容
DOI：
10.1142/9789812831439_0001
发表时间：
1995-04
期刊：
--
影响因子：
--
作者：
K. Fujiwara
通讯作者：
K. Fujiwara
影响因子：
5.7
作者：
J. Peña;M. Larsson;R. I. Merino;I. Francisco;V. Orera;J. Llorca;J. Pastor;A. Martin;J. Segurado-J.
通讯作者：
J. Peña;M. Larsson;R. I. Merino;I. Francisco;V. Orera;J. Llorca;J. Pastor;A. Martin;J. Segurado-J.
DOI：
10.1111/j.1151-2916.1981.tb10321.x
发表时间：
1981-01-01
影响因子：
3.9
作者：
CHANTIKUL, P;ANSTIS, GR;MARSHALL, DB
通讯作者：
MARSHALL, DB
影响因子：
64.8
作者：
Y. Waku;N. Nakagawa;T. Wakamoto;H. Ohtsubo;K. Shimizu;Y. Kohtoku
通讯作者：
Y. Waku;N. Nakagawa;T. Wakamoto;H. Ohtsubo;K. Shimizu;Y. Kohtoku
DOI：
10.1111/j.1151-2916.1981.tb10320.x
发表时间：
1981-01-01
影响因子：
3.9
作者：
ANSTIS, GR;CHANTIKUL, P;MARSHALL, DB
通讯作者：
MARSHALL, DB