Microstructure and mechanical properties of Al2O3/ZrO2 eutectic ceramic composites prepared by explosion synthesis
Microstructure and mechanical properties of Al2O3/ZrO2 eutectic ceramic composites prepared by explosion synthesis
复制标题
爆炸合成Al2O3/ZrO2共晶陶瓷复合材料的显微组织和力学性能
DOI：
10.1016/j.jallcom.2012.11.064
复制
发表时间：
2013-02
影响因子：
6.2
通讯作者：
Yang, Pan
中科院分区：
文献类型：
--
作者：
Zheng, Yong-ting;Li, Hong-Bo;Zhou,Tao;Zhao, Jing;Yang, Pan
以Al和Zr（NO3）4为原料，采用爆炸合成法制备了Al 2 O3/ZrO 2共晶陶瓷。Al 2 O3/ZrO 2共晶组织表明，ZrO 2相呈棒状，直径约200 nm，有序地镶嵌在Al 2 O3基体中。随着反应温度的升高，Al 2 O3/ZrO 2共晶的体积含量相应增加，棒状ZrO 2的直径和相间距减小，这主要归因于较高温度下的充分扩散和较大的过冷度。由于Al 2 O3/ZrO 2共晶组织细小，材料的维氏硬度和断裂韧性分别达到17.7GPa和10.3MPam1/2。
Al2O3/ZrO2eutectic ceramics were prepared by explosion synthesis using Al and Zr(NO3)4as raw materials. The Al2O3/ZrO2eutectic microstructure showed that the rod-like ZrO2phases with a diameter 200nm were embedded orderly in Al2O3matrix. With the increasing of the reaction temperature, the volume content of the Al2O3/ZrO2eutectic increased accordingly, and the diameter and phase spacing of the rod-like ZrO2decreased, which was mainly attributed to the sufficient diffusion at higher temperature and the large degree of supercooling. Due to the fine microstructure of the Al2O3/ZrO2eutectic, the Vickers hardness and fracture toughness can reach 17.7GPa and 10.3MPam1/2, respectively.
登录
查看更多内容
超重力燃烧合成熔铸法制备纳米结构Al2O3/ZrO2（Y2O3）共晶
影响因子：
3
作者：
Mei, Lin;Mai, Peilin;Li, Jiangtao;Chen, Kexin
通讯作者：
Chen, Kexin
影响因子：
1.8
作者：
Mizutani, Y;Yasuda, H;Waku, Y
通讯作者：
Waku, Y
影响因子：
6
作者：
Zhong Zhao;Longyu Zhang;Jian Zheng;H. Bai;Shiyue Zhang;B. Xu
通讯作者：
Zhong Zhao;Longyu Zhang;Jian Zheng;H. Bai;Shiyue Zhang;B. Xu
影响因子：
5.7
作者：
J. Pastor;J. Llorca;P. Poza;I. Francisco;R. I. Merino;J. Peña
通讯作者：
J. Pastor;J. Llorca;P. Poza;I. Francisco;R. I. Merino;J. Peña
影响因子：
1.8
作者：
Lee, JH;Yoshikawa, A;Waku, Y
通讯作者：
Waku, Y