Synthesis and characterizations of Cu2MgSnS4 thin films with different sulfuration temperatures
Synthesis and characterizations of Cu2MgSnS4 thin films with different sulfuration temperatures
复制标题
不同硫化温度Cu2MgSnS4薄膜的合成与表征
DOI：
10.1016/j.matlet.2019.01.102
复制
发表时间：
2019-05
影响因子：
3
通讯作者：
Zhang Zhenzhong
中科院分区：
文献类型：
--
作者：
Yang Gang;Zhai Xiaoli;Li Yongfeng;Yao Bin;Ding Zhanhui;Deng Rui;Zhao Haifeng;Zhang Ligong;Zhang Zhenzhong
Cu2MgSnS4 薄膜采用溶胶-凝胶旋涂法制备，然后进行硫化。研究了退火温度对结构、光学和电学特性的影响。所有退火的 CMTS 薄膜都显示出贫铜和轻微贫硫的情况。 X射线衍射和X射线光电子能谱结果揭示了闪锌矿结构CMTS薄膜的形成。硫化温度的升高提高了CMTS薄膜的结晶度并减小了带隙。 CMTS太阳能电池在530°C的优化温度下表现出0.78%的更高效率。
Cu2MgSnS4thin films were prepared by sol–gel spin-coating route followed by sulfuration. The effects of the annealing temperature on structural, optical and electrical characteristics were investigated. All the annealed CMTS thin films show Cu-poor and slightly S-poor condition. X-ray diffraction and X-ray photoelectron spectroscopy results reveal the formation of zinc-blende structure CMTS thin films. The increase of sulfurization temperature improves the crystallinity and diminishes the bandgaps of CMTS films. The CMTS solar cell shows a better efficiency of 0.78% with the optimized temperature of 530 °C.
登录
查看更多内容
影响因子：
27.8
作者：
Wang, Wei;Winkler, Mark T.;Mitzi, David B.
通讯作者：
Mitzi, David B.
影响因子：
3.2
作者：
Xiangbo Song;Xu Ji;Ming Li;Weidong Lin;Xi Luo;Zhang Hua
通讯作者：
Xiangbo Song;Xu Ji;Ming Li;Weidong Lin;Xi Luo;Zhang Hua
影响因子：
6.9
作者：
M. S. Kumar;Sreejith P. Madhusudanan;Sudip Kumar Batabyal
通讯作者：
M. S. Kumar;Sreejith P. Madhusudanan;Sudip Kumar Batabyal
影响因子：
1.6
作者：
M. Wei;Qingyang Du;Rong Wang;G. Jiang;Weifeng Liu;Changfei Zhu
通讯作者：
M. Wei;Qingyang Du;Rong Wang;G. Jiang;Weifeng Liu;Changfei Zhu
影响因子：
6.9
作者：
C. Cai;Shih-yuan Wei;Wei-Chih Huang;Je-Wei Lin;T. Yeh;C. Lai
通讯作者：
C. Cai;Shih-yuan Wei;Wei-Chih Huang;Je-Wei Lin;T. Yeh;C. Lai