A silica co-electrodeposition route to nanoporous Co3O4 film electrode for oxygen evolution reaction
A silica co-electrodeposition route to nanoporous Co3O4 film electrode for oxygen evolution reaction
复制标题
用于析氧反应的纳米孔 Co3O4 薄膜电极的二氧化硅共电沉积路线
DOI：
10.1016/j.electacta.2013.11.010
复制
发表时间：
2014-01
影响因子：
6.6
通讯作者：
Hu, Ji-Ming
中科院分区：
文献类型：
--
作者：
Wu, Lian-Kui;Hu, Ji-Ming
采用两步法在不锈钢衬底上制备了纳米多孔Co3O4（po-Co3O4）薄膜。首先，将混合溶胶-凝胶前驱体在阴极电位下通过电化学共沉积制备了co3o4 - sio2复合膜。然后，将得到的复合膜在浓KOH溶液中连续循环伏安，刻蚀sio2组分，形成po- co3o4膜。所得膜电极对析氧反应（OER）表现出满意的电催化性能。
Nanoporous Co3O4(po-Co3O4) films have been prepared on stainless steel substrate by a novel two-step method. Firstly, a composite Co3O4-SiO2film was fabricated via electrochemical co-deposition under a cathodic potential from the mixed sol-gel precursor. Then, the obtained composite film was underwent consecutive cycling voltammetries in a concentrated KOH solution to etch the SiO2component, leading to the formation of po-Co3O4films. The resultant film electrode exhibits satisfactory electrocatalytic property towards the oxygen evolution reaction (OER).
登录
查看更多内容
影响因子：
3.9
作者：
P. Nkeng;G. Poillerat;J. Koenig;P. Chartier;B. Lefez;J. Lopitaux;M. Lenglet
通讯作者：
P. Nkeng;G. Poillerat;J. Koenig;P. Chartier;B. Lefez;J. Lopitaux;M. Lenglet
影响因子：
7.2
作者：
C. Bocca;G. Cerisola;E. Magnone;A. Barbucci
通讯作者：
C. Bocca;G. Cerisola;E. Magnone;A. Barbucci
影响因子：
3.7
作者：
Meher, Sumanta Kumar;Rao, G. Ranga
通讯作者：
Rao, G. Ranga
直接获取与一维纳米多孔碳集成的金属或金属氧化物纳米晶体用于电化学储能
影响因子：
15
作者：
Liang, Yanyu;Schwab, Matthias Georg;Muellen, Klaus
通讯作者：
Muellen, Klaus
影响因子：
15
作者：
H. Tüysüz;C. Lehmann;Hans‐Josef Bongard;B. Tesche;R. Schmidt;F. Schüth
通讯作者：
H. Tüysüz;C. Lehmann;Hans‐Josef Bongard;B. Tesche;R. Schmidt;F. Schüth