High-efficiency Cu2O-based heterojunction solar cells fabricated on thermally oxidized copper sheets
High-efficiency Cu2O-based heterojunction solar cells fabricated on thermally oxidized copper sheets
复制标题
热氧化铜片上制备的高效 Cu2O 基异质结太阳能电池
DOI：
10.1109/pvsc.2011.6185896
复制
发表时间：
2011
期刊：
影响因子：
--
通讯作者：
T. Minami
中科院分区：
文献类型：
--
作者：
Y. Nishi;T. Miyata;Jun;T. Minami
通过在热氧化铜片制备的高质量 Cu2O 片上沉积透明导电 AZO 和 ZO 薄膜，制备了低成本的 Al 掺杂 ZnO (AZO)/非掺杂 ZnO (ZO)/Cu2O 异质结太阳能电池，转换效率高达 4.04%。为了实现更高的效率，需要使用低损伤沉积方法在低沉积温度下形成AZO和ZO薄膜。通过脉冲激光沉积在非有意加热的 Cu2O 片上制备了厚度约为 50 nm 的最佳 ZO 薄膜层。
Low cost Al-doped ZnO (AZO)/non-doped ZnO (ZO)/Cu2O heterojunction solar cells with a high conversion efficiency of 4.04% were fabricated by depositing transparent conducting AZO and ZO thin films on high quality Cu2O sheets prepared by thermally oxidizing copper sheets. To achieve higher efficiencies, it is necessary to form the AZO and ZO thin films at a low deposition temperature using a low-damage deposition method. The best ZO thin-film layer was prepared with a thickness around 50 nm on non-intentionally heated Cu2O sheets by a pulsed laser deposition.