Giant magnetic coercivity in YNi4B-type SmNi3TB (T=Mn–Cu) solid solutions
Giant magnetic coercivity in YNi4B-type SmNi3TB (T=Mn–Cu) solid solutions
复制标题
YNi4B型SmNi3TB(T=Mn-Cu)固溶体中的巨磁矫顽力
DOI：
10.1016/j.jmmm.2016.06.034
复制
发表时间：
2016-12
影响因子：
2.7
通讯作者：
A. V. Morozkin
中科院分区：
文献类型：
--
作者：
Chang Yan;V. O. Yapaskurt;A. V. Morozkin
研究了过渡金属取代Ni对SmNi 3 TB（T=Mn，Fe，Co，Cu）固溶体YNi 4 B型SmNi 4 B磁性能的影响。SmNi 4 B、SmNi 3 MnB、SmNi 3FeB、SmNi 3CoB和SmNi 3CuB分别在40 K、210 K、322 K、90 K和57 K出现铁磁有序，在15 K、100 K、185 K、55 K和15 K出现类场敏变磁转变。根据等温磁熵变（ΔSm）计算了SmNi 3 TB（T=Mn-Cu）的磁热效应。在居里温度附近，磁场变化为0-50 kOe时，SmNi 4 B的磁熵Δ Sm在40 K时为-0.94 J/kg K，SmNi 3 MnB的磁熵Δ Sm在205 K时为-1.5 J/kg K，SmNi 3FeB的磁熵Δ Sm在320 K时为-0.54 J/kg K，SmNi 3CoB的磁熵Δ Sm在90 K时为-0.49 J/kg K，SmNi 3CuB的磁熵Δ Sm在60 K时为-0.54 J/kg K。在低温类变磁转变附近，磁场变化为0-50 kOe时，SmNi 4 B、SmNi 3 MnB、SmNi 3FeB、SmNi 3CoB和SmNi 3CuB的Δ Sm分别为+0.71 J/kg K（~ 10 K）、+1.69 J/kg K（~ 30 K）、+0.89 J/kg K（~ 110 K）、+1.08 J/kg K（~ 25 K）和+1.12 J/kg K（~ 10 K）。在磁场诱导转变温度以下，SmNi 3 TB（T=Mn-Cu）表现出巨大的矫顽力，SmNi 4 B在5 K时为74 kOe，SmNi 3 MnB在20 K时为69 kOe（10 K时为90 kOe），SmNi 3FeB在60 K时为77 kOe，SmNi 3CoB在20 K时为88 kOe，SmNi 3CuB在5 K时为52 kOe.
The effects of transition metal substitution for Ni on the magnetic properties of the YNi4B-type SmNi4B via SmNi3TB (T=Mn, Fe, Co, Cu) solid solutions have been investigated. SmNi4B, SmNi3MnB, SmNi3FeB, SmNi3CoB and SmNi3CuB show ferromagnetic ordering at 40 K, 210 K, 322 K, 90 K and 57 K and field sensitive metamagnetic-like transitions at 15 K, 100 K, 185 K, 55 K and 15 K in a magnetic field of 10 kOe, respectively. The magnetocaloric effects of SmNi3TB (T=Mn–Cu) were calculated in terms of isothermal magnetic entropy change (ΔSm). The magnetic entropy ΔSmreaches value of –0.94 J/kg K at 40 K for SmNi4B, –1.5 J/kg K at 205 K for SmNi3MnB, –0.54 J/kg K at 320 K for SmNi3FeB, –0.49 J/kg K at 90 K for SmNi3CoB and –0.54 J/kg K at 60 K for SmNi3CuB in field change of 0–50 kOe around the Curie temperature. They show positive ΔSmof +0.71 J/kg K at ~10 K for SmNi4B, +1.69 J/kg K at 30 K for SmNi3MnB, +0.89 J/kg K at 110 K for SmNi3FeB, +1.08 J/kg K at 25 K for SmNi3CoB and +1.12 J/kg K at 10 K for SmNi3CuB in field change of 0–50 kOe around the low temperature metamagnetic-like transition. Below the field induced transition temperature (change of magnetic structure), SmNi3TB (T=Mn–Cu) exhibits giant magnetic coercivity of 74 kOe at 5 K for SmNi4B, 69 kOe at 20 K (90 kOe at 10 K) for SmNi3MnB, 77 kOe at 60 K for SmNi3FeB, 88 kOe at 20 K for SmNi3CoB and 52 kOe at 5 K for SmNi3CuB.
登录
查看更多内容
影响因子：
1.5
作者：
A. Albinati;B. T. M. Willis
通讯作者：
A. Albinati;B. T. M. Willis
影响因子：
3.2
作者：
Gopalan, R;Ping, DH;Ma, BM
通讯作者：
Ma, BM
DOI：
--
发表时间：
1985-12
期刊：
--
影响因子：
--
作者：
P. Villars;L. D. Calvert
通讯作者：
P. Villars;L. D. Calvert
影响因子：
6.2
作者：
T. Toliński;A. Kowalczyk;A. Szlaferek;B. Andrzejewski;J. Kováč;M. Timko
通讯作者：
T. Toliński;A. Kowalczyk;A. Szlaferek;B. Andrzejewski;J. Kováč;M. Timko
影响因子：
2.2
作者：
P. Villars;K. Cenzual;W. B. Pearson
通讯作者：
P. Villars;K. Cenzual;W. B. Pearson