Microstructure and oxidation resistance of Mo–Si–B coating on Nb based in situ composites
Microstructure and oxidation resistance of Mo–Si–B coating on Nb based in situ composites
复制标题
铌基原位复合材料Mo-Si-B涂层的显微组织和抗氧化性能
DOI：
10.1016/j.corsci.2014.07.006
复制
发表时间：
2014-10
影响因子：
8.3
通讯作者：
Chungen Zhou
中科院分区：
文献类型：
--
作者：
Jingyan Wu;Wan Wang;Chungen Zhou
以Mo-Si-B系两步法涂层为例，对Nb-Si基合金高温抗氧化涂层的发展进行了评价。结果表明，涂层由外层含MoSi2的硼化物弥散体和内层未反应的Mo组成。在1250℃干燥空气中氧化100h后，基体和Mo-Si-B涂层的质量增重率分别为190.08和1.28mgcm−2。涂层良好的抗氧化性归功于形成了连续的硼硅酸盐玻璃覆盖层。
The development of robust high temperature oxidation resistant coatings for Nb–Si based alloy was evaluated for a Mo–Si–B coating system that was applied by a two step process. It is observed that the coating is composed of an outer layer of MoSi2containing boride dispersoids and an inner layer of unreacted Mo. The mass gain of substrate and Mo–Si–B coating is 190.08 and 1.28 mg cm−2after oxidation at 1250 °C in dry air for 100 h, respectively. The good oxidation resistance of the coating is attributed to the formation of a continuous borosilicate glass coverage.
登录
查看更多内容
影响因子：
5.2
作者：
P. R. Taleghani;S. Bakhshi;M. Erfanmanesh;G. H. Borhani;R. Vafaei
通讯作者：
P. R. Taleghani;S. Bakhshi;M. Erfanmanesh;G. H. Borhani;R. Vafaei
DOI：
--
发表时间：
2005
期刊：
--
影响因子：
--
作者：
肖来荣;易丹青;殷磊;蔡志刚
通讯作者：
肖来荣;易丹青;殷磊;蔡志刚
影响因子：
4.4
作者：
Geng, Jie;Tsakiropoulos, Panos
通讯作者：
Tsakiropoulos, Panos
影响因子：
6.7
作者：
Yan-qiang Qiao;Xiping Guo
通讯作者：
Yan-qiang Qiao;Xiping Guo
铌基原位复合材料上锗改性硅化物涂层的形成及其抗氧化性能
影响因子：
8.3
作者：
Wan Wang;Bifei Yuan;Chungen Zhou
通讯作者：
Chungen Zhou