Microstructure and Properties of Electrodeposited Nanocrystalline Ni-Co-Fe Coatings.
Microstructure and Properties of Electrodeposited Nanocrystalline Ni-Co-Fe Coatings.
复制标题
DOI：
10.3390/ma14143886
复制
发表时间：
2021-07-12
期刊：
影响因子：
--
通讯作者：
Dubiel B
中科院分区：
文献类型：
--
作者：
Ledwig P;Kac M;Kopia A;Falkus J;Dubiel B
Materials based on Ni-Co-Fe alloys, due to their excellent magnetic properties, attract great attention in nanotechnology, especially as candidates for high-density magnetic recording media and other applications from spintronic to consumer electronics. In this study, Ni-Co-Fe nanocrystalline coatings were electrodeposited from citrate-sulfate baths with the Ni2+:Co2+:Fe2+ ion concentration ratios equal to 15:1:1, 15:2:1, and 15:4:1. The effect of the composition of the bath on the morphology, microstructure, chemical composition, microhardness, and magnetic properties of the coatings was examined. Scanning (SEM) and transmission (TEM) electron microscopy, X-ray diffractometry (XRD), and energy dispersive X-ray spectroscopy (EDS) were used to study surface morphology, microstructure, chemical, and phase composition. Isothermal cross-sections of the Ni-Co-Fe ternary equilibrium system for the temperature of 50 °C and 600 °C were generated using the FactSage package. Magnetic properties were analyzed by a superconducting quantum interference device magnetometer (SQUID). All the coatings were composed of a single phase being face-centered cubic (fcc) solid solution. They were characterized by a smooth surface with globular morphology and a nanocrystalline structure of grain diameter below 30 nm. It was determined that Ni-Co-Fe coatings exhibit high hardness above 4.2 GPa. The measurements of hysteresis loops showed a significant value of magnetization saturation and small coercivity. The microstructure and properties of the obtained nanocrystalline coatings are interesting in terms of their future use in micromechanical devices (MEMS).
登录
查看更多内容
影响因子：
2.7
作者：
Myung, NV;Park, DY;Sumodjo, PTA
通讯作者：
Sumodjo, PTA
影响因子：
2.3
作者：
Bakhit, Babak;Akbari, Alireza
通讯作者：
Akbari, Alireza
影响因子：
9.4
作者：
Bastos, A.;Zaefferer, S.;Schuh, C.
通讯作者：
Schuh, C.
DOI：
10.1007/s10854-012-1041-x
发表时间：
2013-06-01
影响因子：
2.8
作者：
Kockar, Hakan;Demirbas, Ozen;Alper, Mursel
通讯作者：
Alper, Mursel
影响因子：
1.6
作者：
Divya, V. D.;Ramamurty, U.;Paul, A.
通讯作者：
Paul, A.