Soft magnetic Fe-Si-B-Cu nanocrystalline alloys with high Cu concentrations
Soft magnetic Fe-Si-B-Cu nanocrystalline alloys with high Cu concentrations
复制标题
高浓度 Cu 软磁 Fe-Si-B-Cu 纳米晶合金
DOI：
10.1016/j.jallcom.2017.06.128
复制
发表时间：
2017-10
影响因子：
6.2
通讯作者：
Zhang W.
中科院分区：
文献类型：
--
作者：
Li Y. H.;Jia X. J.;Xu Y. Q.;Chang C. T.;Xie G. Q.;Zhang W.
在高Cu含量的简单Fe-Si-B-Cu合金系中，制备了工艺性好的高饱和磁通密度（Bs）纳米晶软磁合金。对含1.7- 2.0at%Cu的快淬Fe-Si-B-Cu合金进行退火处理，得到了高超导转变温度为1.77T，低矫顽力为1.71A/m的纳米晶合金。高Cu含量有利于在非晶基体中形成平均晶粒尺寸约为1.6 nm的高数密度α-Fe核心，即使在低升温速率退火下，也能通过竞争生长抑制α-Fe晶粒的过度生长，从而获得细小的纳米结构和优异的软磁性能。
High saturation magnetic flux density (Bs) soft magnetic nanocrystalline alloys with good manufacturability were developed in a simple Fe-Si-B-Cu alloy system with high Cu concentrations. The nanocrystalline alloys with highBsof ∼1.77 T and low coercivity of ∼7.1 A/m were obtained by annealing the melt-spun Fe-Si-B-Cu alloys containing 1.7–2.0 at% Cu. The high content of Cu facilitates the formation of high-number-density α-Fe nuclei with an average grain size of ∼6 nm pre-existing in the amorphous matrix, which inhibits the excessive growth of the α-Fe grains by their competitive growth even during the low-heating-rate annealing, resulting in a fine nanostructure and excellent soft magnetic properties.
登录
查看更多内容
影响因子：
3.2
作者：
YOSHIZAWA, Y;OGUMA, S;YAMAUCHI, K
通讯作者：
YAMAUCHI, K
影响因子：
3.2
作者：
Parmanand Sharma;X. Zhang;Yan Zhang;A. Makino
通讯作者：
Parmanand Sharma;X. Zhang;Yan Zhang;A. Makino
影响因子：
3.2
作者：
M. Willard;M. Huang;D. Laughlin;M. McHenry;J. Cross;V. Harris;C. Franchetti
通讯作者：
M. Willard;M. Huang;D. Laughlin;M. McHenry;J. Cross;V. Harris;C. Franchetti
DOI：
10.1002/chin.201314220
发表时间：
2013-02
期刊：
ChemInform
影响因子：
--
作者：
G. Herzer
通讯作者：
G. Herzer
影响因子：
1.2
作者：
Ohta, Motoki;Yoshizawa, Yoshihito
通讯作者：
Yoshizawa, Yoshihito