Micromechanical properties of (Na,Zn)-sulfophosphate glasses
Micromechanical properties of (Na,Zn)-sulfophosphate glasses
复制标题
(Na,Zn)-硫磷酸盐玻璃的微观机械性能
DOI：
10.1016/j.jnoncrysol.2012.01.045
复制
发表时间：
2012
影响因子：
3.5
通讯作者：
L. Wondraczek
中科院分区：
文献类型：
--
作者：
S. Striepe;J. Deubener;L. Wondraczek
采用超声和维氏压痕法测定了含硫磷酸锌钠玻璃的弹性常数、硬度和抗裂性能。在玻璃结构中掺入高达35mol%的硫，导致摩尔体积减少23%，泊松比增加到约0.32。随着玻璃结构的压实，抗永久变形和开裂的能力降低，即在正常气氛下测试时，观察到较软的硫酸盐玻璃具有更脆的特性。在氮气流动条件下，裂纹与压痕尺寸比的组分依赖性较弱，表明表面反应主导了硫酸盐玻璃的微机械裂纹萌生。
Elastic constants, hardness and crack initiation resistance of sulfur-bearing sodium-zinc-phosphate glasses were determined by ultrasonic echography and Vickers indentation experiments. Incorporation of up to 35mol% of sulfur into the glass structure resulted in a decrease in molar volume of 23% and an increase of Poisson's ratio up to a value of~0.32. Resistance against permanent deformation and cracking decreased with compaction of the glass structure, i.e. a more brittle character of softer sulfophosphate glasses was observed when tested under normal atmosphere. Under flowing N2gas only a weak compositional dependence of the crack-to-indent size ratio was evident, which indicates that surface reactions dominate micromechanical crack initiation in sulfophosphate glasses.
登录
查看更多内容
影响因子：
29.4
作者：
Wondraczek, Lothar;Mauro, John C.;Rouxel, Tanguy
通讯作者：
Rouxel, Tanguy
影响因子：
3.9
作者：
N. Ramachandran;D. Shetty
通讯作者：
N. Ramachandran;D. Shetty
在 ZnSO4 -KPO3 - NaPO3 和 Li2SO4 - Na2SO4 - K2SO4 - NaPO3 系统中制造低熔点玻璃
影响因子：
0.6
作者：
V. L. Mmamoshin
通讯作者：
V. L. Mmamoshin
使用裂纹张开位移测量用于牙科修复玻璃陶瓷的基体玻璃的裂纹尖端断裂韧性。
DOI：
10.1016/j.jmbbm.2011.04.016
发表时间：
2011
影响因子：
3.9
作者：
J. Deubener;M. Höland;W. Höland;N. Janakiraman;V. Rheinberger
通讯作者：
V. Rheinberger
压痕尺寸效应：现实还是人为？
影响因子：
4.5
作者：
A. Iost;R. Bigot
通讯作者：
R. Bigot