Green preparation of highly alkali-resistant PTFE composite membranes for advanced alkaline water electrolysis
Green preparation of highly alkali-resistant PTFE composite membranes for advanced alkaline water electrolysis
复制标题
绿色制备先进碱性水电解用高耐碱PTFE复合膜
DOI：
10.1016/j.cej.2021.131340
复制
发表时间：
2021-12
影响因子：
15.1
通讯作者：
Wang Baoguo
中科院分区：
文献类型：
--
作者：
Wan Lei;Xu Ziang;Wang Baoguo
To prepare a hydroxide ion conduction membrane with highly alkaline resistance for advanced alkaline water electrolysis, a large-scale and green preparation strategy that pore-filling polytetrafluoroethylene (PTFE) membrane is proposed to fabricate robust alkaline composite membranes, simultaneously enhance the interfacial compatibility between catalyst layer and membrane in membrane electrode assembly (MEA). Upon the rational design, the PTFE/layered double hydroxide (LDH) composite membranes exhibit good hydroxide conductivity, excellent wettability and exceptional alkaline stability, especially showing no change of the area resistance during 2000 h test in 1 M KOH solution at 60 °C. In advanced alkaline water electrolysis, the MEA with PTFE/LDH composite membranes and precious group metal-free (PGM-free) catalysts specifically showed the voltage of 1.8 V at the current density of 1 A cm−2, while that of commercial Fumasep FAA-3–50 membrane was 2.15 V. The long-term stability is conducted at a current density of 500 mA cm−2for 180 h. Such performance with low-cost and mass-produced PTFE/LDH composite membranes demonstrates that the large-scale and green preparation strategy may drive the development of membranes for advanced alkaline water electrolysis.
登录
查看更多内容
影响因子：
9.5
作者：
Diaz, L. A.;Coppola, R. E.;Ocon, P.
通讯作者：
Ocon, P.
影响因子：
4.6
作者：
Vincent I;Lee EC;Kim HM
通讯作者：
Kim HM
用于燃料电池应用的碱性聚合物电解质超薄复合膜
影响因子：
11.9
作者：
Li, Guangwei;Pan, Jing;Zhuang, Lin
通讯作者：
Zhuang, Lin
影响因子：
4.6
作者：
Lee, Hae In;Dao Thi Dung;Kim, Chang Hee
通讯作者：
Kim, Chang Hee
影响因子：
7.2
作者：
Carbone, A.;Zignani, S. Campagna;Arico, A. S.
通讯作者：
Arico, A. S.