Al2O3/ZrO2 (Y2O3) self-growing composites prepared by combustion synthesis under high gravity
Al2O3/ZrO2 (Y2O3) self-growing composites prepared by combustion synthesis under high gravity
复制标题
超重力燃烧合成制备Al2O3/ZrO2(Y2O3)自生长复合材料
DOI：
10.1016/j.scriptamat.2007.09.051
复制
发表时间：
2008-02
影响因子：
6
通讯作者：
王卫国
中科院分区：
文献类型：
--
作者：
赵忠民;张龙;宋义刚;王卫国
在超重力条件下（> 200 g）采用燃烧合成法制备了Al_2O_3/ZrO_2（Y_2O_3）陶瓷片，陶瓷片由纳米-亚微米t-ZrO_2纤维组成的三角形无序排列的团簇组成，团簇间由微米级t-ZrO_2球形晶粒包围。陶瓷的高强度（接近1.6GPa）归因于小尺寸缺陷和高断裂韧性（接近15.0MPam 1/2），这取决于强烈的耦合增韧机制。
Al2O3/ZrO2(Y2O3) plates were prepared by combustion synthesis under high gravity (>200g) and the ceramics were composed of randomly orientated colonies containing a triangular dispersion of orderly nano-submicrometer t-ZrO2fibers, surrounded by inter-colony regions containing micrometer size t-ZrO2spherical grains. The high strength (close to 1.6GPa) of the ceramics was attributed to small-size defect and high fracture toughness (close to 15.0MPam1/2) dependent on an intensive coupled toughening mechanism.
登录
查看更多内容
影响因子：
6
作者：
Zhong Zhao;Longyu Zhang;Jian Zheng;H. Bai;Shiyue Zhang;B. Xu
通讯作者：
Zhong Zhao;Longyu Zhang;Jian Zheng;H. Bai;Shiyue Zhang;B. Xu
影响因子：
5.7
作者：
J. Pastor;J. Llorca;P. Poza;I. Francisco;R. I. Merino;J. Peña
通讯作者：
J. Pastor;J. Llorca;P. Poza;I. Francisco;R. I. Merino;J. Peña
影响因子：
5.7
作者：
L. Mazerolles;D. Michel;M. Hÿtch
通讯作者：
L. Mazerolles;D. Michel;M. Hÿtch
DOI：
10.1016/s0921-5093(00)02040-2
发表时间：
2001-06-30
影响因子：
6.4
作者：
Pastor, JY;Poza, P;Orera, VM
通讯作者：
Orera, VM
影响因子：
5.7
作者：
Larrea, A;de la Fuente, GF;Orera, VM
通讯作者：
Orera, VM