High strain rate indentation-induced deformation in alumina ceramics measured by Cr3+ fluorescence mapping
High strain rate indentation-induced deformation in alumina ceramics measured by Cr3+ fluorescence mapping
复制标题
通过 Cr3 荧光映射测量氧化铝陶瓷中高应变率压痕引起的变形
DOI：
10.1016/j.jeurceramsoc.2011.06.002
复制
发表时间：
2011
影响因子：
5.7
通讯作者：
Dancer C
中科院分区：
文献类型：
--
作者：
Dancer C
氧化铝材料的晶粒尺寸和纯度的范围内进行了小规模的动态冲击由尖锐的碳化钨弹丸在亚弹道速度。通过目视检查受冲击表面上的裂纹和次表面区域中的损坏来记录材料的抗断裂性。使用Cr3+荧光图谱检查每种材料中引起的残余应力和塑性变形。一个修改后的赫兹压痕模型的应力状态的材料中添加一个水泡场表示的应力引起的存在下的塑性区被发现准确地描述所观察到的裂纹下的材料的表面，以及表面上的径向裂纹。
Alumina materials with a range of grain sizes and purities were subjected to small-scale dynamic impact by sharpened tungsten carbide projectiles at sub-ballistic velocities. The resistance of the materials to fracture was recorded by visual examination of the cracking on the impacted surface and the damage in the subsurface region. The residual stress and plastic deformation induced in each material were examined using Cr3+fluorescence mapping. A modified Hertzian indentation model of the stress state in the material with the addition of a blister field representing the stress induced by the presence of the subsurface plastic zone was found accurately describe the observed cracks beneath the surface of the material, as well as the radial cracks on the surface.
登录
查看更多内容
微观结构规模对 Al2O3 抗冲击性能的影响
DOI：
--
发表时间：
1993
期刊：
影响因子：
--
作者：
R. Anderson;T. Adler;J. Hawk
通讯作者：
J. Hawk
在光学微探针中使用荧光测量应力：掺铬蓝宝石中压痕周围的应力
影响因子：
3.9
作者：
S. Molis;D. Clarke
通讯作者：
D. Clarke
影响因子：
3.2
作者：
D. Munson;R. Lawrence
通讯作者：
D. Munson;R. Lawrence
用于表征延展性金属和合金的高应变率塑性流动行为的动态压痕技术
DOI：
--
发表时间：
1991
期刊：
影响因子：
--
作者：
Y. Tirupataiah;G. Sundararajan
通讯作者：
G. Sundararajan
发掘新的高度适应性化合物
DOI：
--
发表时间：
2007
期刊：
影响因子：
--
作者：
James D. Sawyer
通讯作者：
James D. Sawyer