Fabrication and laser output of transparent Nd:YAG ceramics from microwave synthesized precursors
Fabrication and laser output of transparent Nd:YAG ceramics from microwave synthesized precursors
复制标题
微波合成前驱体透明 Nd:YAG 陶瓷的制造和激光输出
DOI：
10.1007/s12598-011-0437-8
复制
发表时间：
2011-12
期刊：
影响因子：
8.8
通讯作者：
Liu Hong
中科院分区：
文献类型：
--
作者：
Zhang Xiaolin;Liu Duo;Wang Jiyang;Yu Haohai;Qin Haiming;Sang Yuanhua;Liu Hong
报道了用微波辅助均相沉淀法(MAHP)制备透明的Nd：Y3Al5O12陶瓷的激光输出。在温度为25℃、湿度为30%~50%的条件下，对经过6d老化处理的前驱体颗粒进行热处理，得到了平均粒径小于100 nm的纯相、均匀的纳米粉末，并在1730℃下真空烧结10h，获得了斜率效率为5.1%的激光输出(305 MW)。我们的结果表明，MAHP方法有可能用于激光陶瓷产品的制备。
We report the laser output of transparent Nd:YAG (Nd:Y3Al5O12) ceramics fabricated from Nd:YAG precursors through the microwave-assisted homogenous precipitation (MAHP) method. Pure phase and uniform Nd:YAG nano-powders with average sizes less than 100 nm were obtained by heating treatment of the Nd:YAG precursor particles aged for 6 d in vessel with humidity of 30%–50% at 25°C. Transparent Nd:YAG ceramic pellets were obtained by vacuum sintering at 1730°C for 10 h. Laser output (305 mW) with a slope efficiency of 5.1% was realized through an end-pumped configuration. Our results indicate that the MAHP method could potentially be used for the fabrication of laser ceramic products.
登录
查看更多内容
影响因子：
3.9
作者：
H. Yagi;T. Yanagitani;K. Takaichi;K. Ueda;A. Kaminskii
通讯作者：
H. Yagi;T. Yanagitani;K. Takaichi;K. Ueda;A. Kaminskii
DOI：
10.1109/cleo.2007.4452868
发表时间：
2006-06
期刊：
2007 Conference on Lasers and Electro-Optics (CLEO)
影响因子：
--
作者：
A. Ikesue;Y. Aung
通讯作者：
A. Ikesue;Y. Aung
影响因子：
6.2
作者：
Lu, JR;Ueda, K;Kaminskii, AA
通讯作者：
Kaminskii, AA
影响因子：
6.2
作者：
Zuogui Wu;Xudong Zhang;Wen He;Yuanwei Du;N. Jia;Pengcheng Liu;Fan-Yu Bu
通讯作者：
Zuogui Wu;Xudong Zhang;Wen He;Yuanwei Du;N. Jia;Pengcheng Liu;Fan-Yu Bu
影响因子：
6.2
作者：
Xiaoli Zhang;Duo Liu;Y. Sang;Hong Liu;Ji-yang Wang
通讯作者：
Xiaoli Zhang;Duo Liu;Y. Sang;Hong Liu;Ji-yang Wang