表面氧化层破裂以及随后暴露的清洁金属表面对于粉末固结和增材制造的各种固态工艺至关重要。我们通过在扫描电子显微镜内使单个球形粉末颗粒变形来解决这个过程。我们揭示了三种断裂模式，即子午线、径向和周向裂纹，它们依次随着颗粒压扁而激活。颗粒压扁时负载和位移的实时测量也揭示了表面氧化物的显着强化效应。我们将强化归因于两种机制：复合强化和应变梯度强化。
Surface oxide layer fracture and the subsequent exposure of clean metallic surfaces are critical in various solid-state processes for powder consolidation and additive manufacturing. We resolve this processin-situby deforming individual spherical powder particles inside a scanning electron microscope. We reveal three fracture modalities, i.e., meridian, radial, and circumferential cracking that sequentially activate with particle flattening. Real time measurements of load and displacement upon particle flattening also reveal a significant strengthening effect by surface oxide. We attribute the strengthening to two mechanisms: the composite strengthening and the strain gradient strengthening.
登录
查看更多内容
DOI：
--
发表时间：
2012
期刊：
Journal of thermal spray technology (Print)
影响因子：
--
作者：
Minyxiang Yu;Wenya Li;Xueping Guo;H. Liao
通讯作者：
H. Liao
铝低温位错弛豫的指前因子和活化能的测定
DOI：
--
发表时间：
2000
期刊：
影响因子：
--
作者：
H. Koizumi;T. Koizumi;T. Kosugi
通讯作者：
T. Kosugi
影响因子：
3.6
作者：
A. A. Ward-A.;Christopher A. Hareland;Nathan E. Palmerio;Z. Cordero
通讯作者：
A. A. Ward-A.;Christopher A. Hareland;Nathan E. Palmerio;Z. Cordero
影响因子：
6.7
作者：
Hassani-Gangaraj, Mostafa;Veysset, David;Schuh, Christopher A.
通讯作者：
Schuh, Christopher A.
固体颗粒沉积过程中结合机制统一认识的现状与挑战
DOI：
--
发表时间：
2021
期刊：
影响因子：
--
作者：
Y. Ichikawa;K. Shinoda
通讯作者：
K. Shinoda