Improving Corrosion Resistance of Ferrous Alloy to Molten Zn by Modifying the Laves Phase Characteristics
Improving Corrosion Resistance of Ferrous Alloy to Molten Zn by Modifying the Laves Phase Characteristics
复制标题
通过改变Laves相特性提高铁合金对熔融锌的耐蚀性
DOI：
10.1007/s11837-017-2493-5
复制
发表时间：
2018-11
期刊：
影响因子：
--
通讯作者：
Jia Lou
中科院分区：
文献类型：
--
作者：
Xin Liu;Fucheng Yin;Xuemei Ouyang;Zhi Li;Jia Lou
Fe25Mo14Cr10Ni1Si（wt.%）中的Laves相形貌为提高铁基合金的耐锌液腐蚀性能，对铁基合金进行了Si变质处理。含Si合金表现出编织的针状Laves相，其Mo含量高于Fe25Mo14Cr10Ni合金。含硅合金对熔融锌的耐腐蚀性比不含硅合金高20倍以上，这主要是由于改性Laves相的特性。该相的取向垂直于Zn扩散方向，这有效地防止了熔融Zn的腐蚀，导致更致密的FeZn 13层，而不是在Fe 25Mo 14Cr 10Ni合金中产生的FeZn 10层。
The Laves phase morphology in the Fe25Mo14Cr10Ni1Si (wt.%) alloy was modified by Si addition to improve the corrosion resistance of the ferrous alloy to molten zinc. The Si-containing alloy showed a woven, needle-like Laves phase with higher Mo content than that of the Fe25Mo14Cr10Ni alloy. Corrosion resistance to molten Zn for the Si-containing alloy was more than 20 times higher than that of the silicon-free alloy mainly as a result of the characteristics of the modified Laves phase. This phase was oriented perpendicular to the Zn-diffusion direction, which effectively prevented corrosion by the molten Zn, leading to a denser FeZn13layer rather than the FeZn10layer produced in the Fe25Mo14Cr10Ni alloy.
登录
查看更多内容
DOI：
10.1007/s11661-005-0325-7
发表时间：
2005-08-01
影响因子：
2.8
作者：
Liu, XB;Barbero, E;Sikka, V
通讯作者：
Sikka, V
钼对铸态Fe-B合金组织及锌液耐蚀性能的影响
影响因子：
1.6
作者：
Ouyang, Xuemei;Chen, Guopeng;Zhao, Manxiu
通讯作者：
Zhao, Manxiu
影响因子：
8.3
作者：
Ma, Shengqiang;Xing, Jiandong;Ma, Shengchao
通讯作者：
Ma, Shengchao
影响因子：
5
作者：
K. Zhang
通讯作者：
K. Zhang
影响因子：
9.4
作者：
Aghajani, A.;Somsen, Ch.;Eggeler, G.
通讯作者：
Eggeler, G.