Thermal stability and thermal shock resistance of Fe2AlB2
Thermal stability and thermal shock resistance of Fe2AlB2
复制标题
Fe2AlB2的热稳定性和抗热震性能
DOI：
10.1016/j.ceramint.2018.06.042
复制
发表时间：
2018-09
影响因子：
5.2
通讯作者：
Zhou Yang
中科院分区：
文献类型：
--
作者：
Liu Jie;Li Shibo;Yao Boxiang;Zhang Jing;Lu Xiaogang;Zhou Yang
纳米三元硼化物Fe2AlB2在室温下表现出损伤容限、导电性和可加工性的组合。本工作首次报道了Fe2AlB2的高温热稳定性和抗热震性。研究了Fe_2AlB_2在Ar气氛中的热稳定性，最高温度为1300 °C。在Ar气氛中，Fe2AlB2在1236 °C下发生强烈分解。在600~1200 °C温度范围内，采用水淬法研究了Fe2AlB2的抗热震性。用X射线衍射仪、差示扫描量热仪和扫描电子显微镜对其物相组成、相变和微观结构进行了表征。
The nanolaminated ternary boride Fe2AlB2exhibits a combination of damage tolerance, electrical conductivity, and machinability at room temperature. This work reports for the first time on the thermal stability and thermal shock resistance of Fe2AlB2at high temperatures. The thermal stability of Fe2AlB2at temperatures up to 1300 °C in Ar atmosphere was studied. Fe2AlB2intensively decomposed at 1236 °C in Ar atmosphere. The thermal shock resistance was investigated using the water-quenching method in the temperature range 600–1200 °C. The residual strength of the quenched Fe2AlB2decreased continuously with increasing temperatures. The phase composition, phase transformation and microstructure were characterized with X-ray diffractometry, differential scanning calorimetry and scanning electron microscopy.
登录
查看更多内容
Cr2AlC的合成及热稳定性
DOI：
10.1016/j.jeurceramsoc.2011.01.009
发表时间：
2011-07
期刊：
Journal of European Ceramic Society
影响因子：
--
作者：
李世波
通讯作者：
李世波
影响因子：
3.3
作者：
Yan Cheng;Zhen‐Long Lv;Xiang-Rong Chen;L. Cai
通讯作者：
Yan Cheng;Zhen‐Long Lv;Xiang-Rong Chen;L. Cai
单质粉末机械活化烧结Ti3AlC2的合成及微观结构
影响因子：
5.2
作者：
Zhang, Zhi-Li;Zhou, Yang;Li, Shi-Bo;Bei, Guo-Ping;Zhai, Hong-Xiang
通讯作者：
Zhai, Hong-Xiang
影响因子：
1.8
作者：
Y. Bao;C. Hu;Y. Zhou
通讯作者：
Y. Bao;C. Hu;Y. Zhou
影响因子：
15
作者：
Tan, Xiaoyan;Chai, Ping;Shatruk, Michael
通讯作者：
Shatruk, Michael