Novel morphologies of intermetallic phases in Sn-Ni peritectic alloys
Novel morphologies of intermetallic phases in Sn-Ni peritectic alloys
复制标题
Sn-Ni包晶合金中金属间相的新形态
DOI：
10.1016/j.matlet.2017.04.091
复制
发表时间：
2017-08
影响因子：
3
通讯作者：
Li JianGong
中科院分区：
文献类型：
--
作者：
Peng Peng;Li XinZhong;Li JianGong
锡镍包晶合金经过深酸腐蚀后，观察到了成分范围较窄的金属间化合物相的新形态。初生Ni3Sn2相和包晶Ni3Sn4相都是成分范围较窄的金属间化合物，而包晶Ni3Sn4相的成分范围较大。虽然可以观察到初生Ni3Sn2相的枝晶生长，但它们是由细小的刻面亚结构组成的。此外，还证实了包晶Ni3Sn4相在恒定生长速度下发生了从面状到非面状的形态转变。这些发现有助于金属间化合物相的生长控制。
The novel morphologies of intermetallic phases with narrow composition ranges are observed in Sn-Ni peritectic alloys after experiencing deep acid etching. Both the primary Ni3Sn2and peritectic Ni3Sn4phases are intermetallic compounds with narrow composition ranges, and the former one has a larger range. Although dendritic growth of primary Ni3Sn2phases can be observed, they are shown to be composed of small faceted sub-structures. In addition, a faceted to non-faceted morphology transition of peritectic Ni3Sn4phase which is observed at a constant growth velocity is also confirmed. These finds are helpful for growth control of intermetallic phases.
登录
查看更多内容
影响因子：
16.1
作者：
H. W. Kerr;W. Kurz
通讯作者：
H. W. Kerr;W. Kurz
影响因子：
2.7
作者：
Huijun Kang;Tongmin Wang;Xinzhong Li;Yan-Qing Su;Jingjie Guo;H. Fu
通讯作者：
Huijun Kang;Tongmin Wang;Xinzhong Li;Yan-Qing Su;Jingjie Guo;H. Fu
影响因子：
4.5
作者：
P. Peng;Jieren Yang;Xinzhong Li;Yan-Qing Su;Jingjie Guo;H. Fu
通讯作者：
P. Peng;Jieren Yang;Xinzhong Li;Yan-Qing Su;Jingjie Guo;H. Fu
影响因子：
4.5
作者：
B. Straumal;O. Kogtenkova;A. Gornakova;V. Sursaeva;B. Baretzky
通讯作者：
B. Straumal;O. Kogtenkova;A. Gornakova;V. Sursaeva;B. Baretzky
影响因子：
6.2
作者：
P. Peng;Xinzhong Li;Yan-Qing Su;Jiangong Li;Jingjie Guo;H. Fu
通讯作者：
P. Peng;Xinzhong Li;Yan-Qing Su;Jiangong Li;Jingjie Guo;H. Fu