Amine, Melamine, and Amide N-Halamines as Antimicrobial Additives for Polymers.
Amine, Melamine, and Amide N-Halamines as Antimicrobial Additives for Polymers.
复制标题
DOI：
10.1021/ie101519u
复制
发表时间：
2010
影响因子：
4.2
通讯作者：
Sun, Yuyu
中科院分区：
文献类型：
--
作者：
Sun, Xinbo;Cao, Zhengbing;Porteous, Nuala;Sun, Yuyu
以2，2，6，6-四甲基-4-哌啶醇盐酸盐(TMP·HCl)为原料，与月桂酰氯反应，再用二氯异氰尿酸钠进行氯化反应，制得N-氯-2，2，6，6-四甲基-4-哌啶醇月桂酸酯(CL-TMPL)。用红外光谱、核磁共振、差示扫描量热法和热重分析对其化学结构进行了表征。比较了氯-TMPL与1-氯-3-十二烷基-5，5-二甲基海因(Cl-DDMH)和氯-2，4-二氨基-6-十二烷基-1，3，5-三嗪(CI-DADT)对革兰氏阳性菌和革兰氏阴性菌的抑菌性能。将这三类N-卤胺用作聚氨酯(PU)的添加剂。可见光透过率实验表明，高达6%的Cl-DDMH或Cl-DADT可与PU相容，但在高于2%时，Cl-TMPL与PU的相容性较差。在添加剂含量相同的情况下，Cl-DDMH和Cl-DADT的抑菌效果和生物被膜控制效果均强于Cl-TMPL。然而，在稳定性研究中，含有Cl-TMPL的PU样品向浸泡液中释放的活性氯量最低，这表明抗菌和生物被膜控制效果的稳定性最高。
N-chloro-2,2,6,6-tetramethyl-4-piperidinol laurate (Cl-TMPL) was prepared by reacting 2,2,6,6-tetramethyl-4-piperidinol hydrochloride (TMP·HCl) with lauroyl chloride, followed by chlorination with sodium dichloroisocyanurate. The chemical structure of Cl-TMPL was characterized with FT-IR, NMR, DSC, and TGA analyses. The antimicrobial performance of Cl-TMPL against Gram-positive and Gram-negative bacteria was compared with 1-chloro-3-dodecyl-5,5-dimethylhydantoin (Cl-DDMH), a amide N-halamine, and chloro-2,4-diamino-6-dodecyl-1,3,5-triazine (Cl-DADT), a melamine (imino) N-halamine. The three classes of N-halamines were used as additives for polyurethane (PU). Visible light transparency data indicated that up to 6% of Cl-DDMH or Cl-DADT could be compatibly mixed with PU, but Cl-TMPL had low compatibility with PU at higher than 2% of Cl-TMPL. With the same additive content, Cl-DDMH and Cl-DADT provided more powerful antimicrobial and biofilm-controlling effects than Cl-TMPL. In stability studies, however, PU samples with Cl-TMPL released the lowest amount of active chlorine into the immersing solution, suggesting the highest stability of the antimicrobial and biofilm-controlling efficacy.
登录
查看更多内容
DOI：
10.1016/j.msec.2010.03.004
发表时间：
2010-06-15
影响因子：
7.9
作者：
Dagostin, V. S.;Golcalves, D. L.;Fiori, M. A.
通讯作者：
Fiori, M. A.
DOI：
10.1002/pola.1992.080300604
发表时间：
1992-05-01
影响因子：
--
作者：
LEE, CS;LAU, WWY;GOH, SH
通讯作者：
GOH, SH
影响因子：
2.1
作者：
ZAKRZEWSKI, J
通讯作者：
ZAKRZEWSKI, J
影响因子：
5.5
作者：
Chen, ZB;Sun, YY
通讯作者：
Sun, YY
影响因子：
2.4
作者：
Wiese, A;Münstermann, M;Seydel, U
通讯作者：
Seydel, U