Preparation and characterization of novel structure Co–B hydrogen storage alloy
Preparation and characterization of novel structure Co–B hydrogen storage alloy
复制标题
新型结构Co-B储氢合金的制备及表征
DOI：
10.1016/j.elecom.2008.07.034
复制
发表时间：
2008-10
影响因子：
5.4
通讯作者：
中科院分区：
文献类型：
--
作者：
采用化学还原法和退火法制备Co-B合金。使用 TEM 和 XRD 进行结构和形态表征。使用 LAND 电池测试仪器进行电化学测量。退火处理后,初始Co-B合金分解为具有涂层球结构的晶态Co和B。还获得了优异的电化学储氢性能。
The Co–B alloy was prepared by the chemical reduction method and the annealing method. The structural and morphological characterizations were performed using TEM and XRD. The Electrochemical Measurements were performed using LAND battery test instrument. After annealing treatment,the initial Co–B alloy decomposes to crystalline Co and B with a kind of coating sphere structure. The excellent electrochemical hydrogen storage properties are also obtained.
登录
查看更多内容
DOI：
10.1016/s0927-7757(98)00398-7
发表时间：
1999-04
期刊：
Colloids and Surfaces A: Physicochemical and Engineering Aspects
影响因子：
--
作者：
M. Mitov;A. Popov;I. Dragieva
通讯作者：
M. Mitov;A. Popov;I. Dragieva
影响因子：
6.2
作者：
M. Jurczyk
通讯作者：
M. Jurczyk
影响因子：
6.2
作者：
Jing-Wang Liu;H. Yuan;Jian-sheng Cao;Yijing Wang
通讯作者：
Jing-Wang Liu;H. Yuan;Jian-sheng Cao;Yijing Wang
影响因子：
64.8
作者：
Dillon, AC;Jones, KM;Heben, MJ
通讯作者：
Heben, MJ
影响因子：
15
作者：
K. Raghavachari;Q. Fu;Gang Chen;Liang-Shi Li;Li Ch;Law Dc;Robert F. Hicks
通讯作者：
K. Raghavachari;Q. Fu;Gang Chen;Liang-Shi Li;Li Ch;Law Dc;Robert F. Hicks