Scintillation properties of Ce- and Eu-doped Ca2MgSi2O7 crystals
Scintillation properties of Ce- and Eu-doped Ca2MgSi2O7 crystals
复制标题
Ce 和 Eu 掺杂 Ca2MgSi2O7 晶体的闪烁特性
DOI：
10.1016/j.optmat.2018.12.056
复制
发表时间：
2019
影响因子：
3.9
通讯作者：
Yanagida Takayuki
中科院分区：
文献类型：
--
作者：
Ogawa Taiki;Nakauchi Daisuke;Okada Go;Kawaguchi Noriaki;Yanagida Takayuki
采用浮区法制备了掺Ce和Eu的Ca2MgSi2O7(CMSM)单晶。从X-射线衍射图可以看出，所有的CMSM样品都没有杂质相。在X射线辐照下，掺Ce和掺Eu的CMSM样品分别在390 nm和530 nm附近有较宽的发射。这些发射的来源被认为分别是Ce3+和Eu2+的5d-4f跃迁。在241Amγ-ray(59.5keV)下，掺Eu的CMSM样品的绝对光产额为11,000nph/MeV。此外，Ce和Eu掺杂样品的余辉特性与相应的热释光特性一致。
Ce- and Eu-doped Ca2MgSi2O7(CMSM) single crystals were synthesized by the Floating Zone method. From the X-ray diffraction patterns, we confirmed that all the CMSM samples have no impurity phases. Under X-ray irradiation, the Ce- and Eu-doped CMSM samples showed scintillation with a broad emission around 390 nm and 530 nm, respectively. The origin of these emissions was considered to be the 5d-4f transitions of Ce3+and Eu2+, respectively. The absolute light yield of the Eu-doped CMSM sample was 11,000 ph/MeV evaluated under241Am γ-ray (59.5 keV). In addition, afterglow properties of the Ce- and Eu-doped samples were consistent with the corresponding thermoluminescence properties.
登录
查看更多内容
TlSr2I5(Eu2)单晶的闪烁性能
影响因子：
3.9
作者：
H. Kim;G. Rooh;A. Khan;H. Park;Sunghwan Kim
通讯作者：
Sunghwan Kim
DOI：
10.1016/0168-583x(89)90622-8
发表时间：
1989-04-01
影响因子：
1.3
作者：
MELCHER, CL
通讯作者：
MELCHER, CL
AlN 的剂量计特性
DOI：
--
发表时间：
2013
期刊：
影响因子：
--
作者：
T. Yanagida;Y. Fujimoto;N. Kawaguchi;S. Yanagida
通讯作者：
S. Yanagida
影响因子：
3.5
作者：
Birkel, Alexander;Darago, Lucy E.;Seshadri, Ram
通讯作者：
Seshadri, Ram
正交晶系Gd2Si2O7测井高温闪烁特性
影响因子：
2.3
作者：
Youichi Tsubota;J. Kaneko;M. Higuchi;S. Nishiyama;H. Ishibashi
通讯作者：
H. Ishibashi