Direct fabrication of bimodal mesoporous carbon by nanocasting
Direct fabrication of bimodal mesoporous carbon by nanocasting
复制标题
纳米铸造直接制备双峰介孔碳
DOI：
10.1016/j.micromeso.2008.03.018
复制
发表时间：
2008-12
影响因子：
5.2
通讯作者：
中科院分区：
文献类型：
--
作者：
采用简单的一步模板法成功制备了双峰介孔碳。在我们的方法中，大介孔模板是由多余的二氧化硅框架在干燥诱导下坍塌而原位形成的二氧化硅纳米团块。此外，通过甲基化β-环糊精与正硅酸四甲基（CD/TMOS）的比例可以很容易地定制大介孔的直径，并且随着CD/TMOS的降低而增加。典型的双峰介孔碳具有直径为2.4nm和约24nm的介孔，具有较大的brunauer - emmet - teller表面积（如783m2/g）和较大的介孔体积（如2.18cm3/g）。
Bimodal mesoporous carbons were successfully prepared by a simple one-step templating method. The template of large mesopores in our method is the in situ formed silica nano-agglomerate from the drying-induced collapse of superfluous silica frameworks. Moreover, the diameter of large mesopores can be easily tailored by the ratio of methylated β-cyclodextrin to tetramethyl orthosilicate (CD/TMOS), increasing with decreasing the CD/TMOS. The typical bimodal mesoporous carbons with 2.4nm and ca. 24nm diameter mesopores have great Brunauer–Emmett–Teller surface areas (e.g. 783m2/g) and large mesopore volumes (e.g. 2.18cm3/g).
登录
查看更多内容
影响因子：
--
作者：
Z. Yuan;B. Su
通讯作者：
Z. Yuan;B. Su
影响因子：
10.9
作者：
Böhme, K;Einicke, WD;Klepel, O
通讯作者：
Klepel, O
影响因子：
29.4
作者：
Akira Taguchi;J. Smått;Mika Lindén
通讯作者：
Akira Taguchi;J. Smått;Mika Lindén
影响因子：
29.4
作者：
N. Camaioni;G. Ridolfi;G. Casalbore-Miceli;G. Possamai;M. Maggini
通讯作者：
N. Camaioni;G. Ridolfi;G. Casalbore-Miceli;G. Possamai;M. Maggini
影响因子：
8.6
作者：
B. Su;A. Vantomme;L. Surahy;R. Pirard;J. Pirard
通讯作者：
B. Su;A. Vantomme;L. Surahy;R. Pirard;J. Pirard