Thermal shock behavior of Cr2AlC in different quenching media
Thermal shock behavior of Cr2AlC in different quenching media
复制标题
Cr2AlC在不同淬火介质中的热震行为
DOI：
10.1016/j.matlet.2015.12.160
复制
发表时间：
2016-03
影响因子：
3
通讯作者：
Zhou Yang
中科院分区：
文献类型：
--
作者：
Li Haolin;Li Shibo;Du Xuesong;Bao Peiwei;Zhou Yang
Many ternary ceramics exhibit an abnormal thermal shock behavior as quenched in water. It is not clear that the unique thermal shock behavior remains valid during quenching in other quenching media. This work reports on the investigation of the thermal shock behavior of Cr2AlC as a representative member of the ternary ceramics in various quenching media. The quenching tests revealed that the abnormal thermal shock behavior of Cr2AlC was observed during quenching in water, oil and molten salt. Crack healing is the main mechanism responsible for the unusual thermal shock behavior.
登录
查看更多内容
Cr2AlC的合成及热稳定性
DOI：
10.1016/j.jeurceramsoc.2011.01.009
发表时间：
2011-07
期刊：
Journal of European Ceramic Society
影响因子：
--
作者：
李世波
通讯作者：
李世波
影响因子：
6.2
作者：
I. Salama;T. El-Raghy;M. Barsoum
通讯作者：
I. Salama;T. El-Raghy;M. Barsoum
DOI：
10.1016/j.jeurceramsoc.2004.08.026
发表时间：
2005-09-01
影响因子：
5.7
作者：
Bao, YW;Wang, XH;Zhou, YC
通讯作者：
Zhou, YC
影响因子：
6.2
作者：
A. Ganguly;T. Zhen;M. Barsoum
通讯作者：
A. Ganguly;T. Zhen;M. Barsoum
影响因子：
3.9
作者：
Lin, Zhijun;Li, Meishuan;Zhou, Yanchun
通讯作者：
Zhou, Yanchun