High pressure floating-zone growth and property characterization of Cr-doped hexagonal YMnO3 crystals
High pressure floating-zone growth and property characterization of Cr-doped hexagonal YMnO3 crystals
复制标题
Cr掺杂六方YMnO3晶体的高压浮区生长及性能表征
DOI：
10.1016/j.jmst.2017.04.014
复制
发表时间：
2017-10
影响因子：
10.9
通讯作者：
Cao Chongde
中科院分区：
文献类型：
--
作者：
Wan Feng;Bai Xiaojun;Song Kaikai;Zheng Jianbang;Lin Xin;Cao Chongde
用高压光学浮区法生长了掺Cr的YMnO_3单晶。生长的晶体的尺寸通常为60-70 mm长和4-5 mm直径。通过粉末X射线衍射和扫描电子显微镜分析了生长的晶体的结构。研究了晶体生长过程中的缺陷，包括小角度晶界和夹杂物。不同部位存在轻微的缺铬现象。讨论了晶体生长过程中缺陷与生长条件的关系。在30 K以下，样品的磁性表现为自旋玻璃相特征，具有弱铁磁行为。
Large crystal growth of Cr-dopedh-YMnO3has been investigated by using a high pressure optical floating-zone method. The size of the grown crystals is typically 60–70 mm in length and 4–5 mm in diameter. The structure of the grown crystals is analyzed by powder X-ray diffraction and scanning electron microscopy. The defects in the as-grown crystals, including low-angle grain boundary and inclusions are studied. An off-stoichiometric phenomenon is found with a slight Cr deficiency in different parts. The relationship between defects and growth conditions during crystal growth is also discussed. The magnetic properties show spin-glass phase features with weak ferromagnetic behavior below 30 K.
登录
查看更多内容
DOI：
10.1088/0953-8984/24/23/235402
发表时间：
2012-06
期刊：
Journal of Physics: Condensed Matter
影响因子：
--
作者：
N. Jiang;X. Zhang
通讯作者：
N. Jiang;X. Zhang
影响因子：
3.7
作者：
S. Mori;J. Tokunaga;Y. Horibe;Y. Aikawa;T. Katsufuji
通讯作者：
S. Mori;J. Tokunaga;Y. Horibe;Y. Aikawa;T. Katsufuji
影响因子：
3.2
作者：
R. Thakur;R. Thakur;S. Samatham;N. Kaurav;V. Ganesan;N. Gaur;G. Okram
通讯作者：
R. Thakur;R. Thakur;S. Samatham;N. Kaurav;V. Ganesan;N. Gaur;G. Okram
影响因子：
8.6
作者：
Cho, D.-Y.;Kim, J.-Y.;Jo, T.
通讯作者：
Jo, T.
影响因子：
1.9
作者：
A. Zhang;W. Zhu;X. S. Wu;Q. Bian
通讯作者：
A. Zhang;W. Zhu;X. S. Wu;Q. Bian