Temperature Compensation of Bonded Rare-Earth Magnets by Blending of Alloy Powders (Materials Research)

通过混合合金粉末对粘结稀土磁体进行温度补偿（材料研究）

• 批准号: 8760725
• 负责人: Reinhold Strnat
• 金额: $ 4.96万
• 依托单位: KJS Associates, Inc.
• 依托单位国家: 美国
• 项目类别: Standard Grant
• 财政年份: 1988
• 资助国家: 美国
• 起止时间: 1988-02-01 至 1988-07-31
• 项目状态: 已结题
• 来源: https://www.nsf.gov/awardsearch/showAward?AWD_ID=8760725&HistoricalAwards=false
• 关键词: Temperature; Compensation; Bonded; Rare; Earth

This proposal will examine a method of internal temperature compensation in bonded rare-earth permanent magnets. Emphasis will be on neodymium-iron-boron magnets, which have a strong temperature dependence of the spontaneous magnetization in the range of 0 to +150 C. Coarse powders of the main magnetic constituent will be blended with a second hard magnetic material that displays an opposite temperature coefficient of magnetization. Suitable alloy compositions will be identified, a model developed, and blends tested in Phase I.

本提案将研究一种测量内部温度的方法 粘结稀土永磁体的补偿。 重点 将在钕铁硼磁铁，其中有一个强大的 的自发磁化的温度依赖性 温度范围为0至+150 ℃。 主要磁性材料的粗粉 成分将与第二硬磁材料混合 显示出相反的温度系数 磁化 将确定合适的合金组成， 开发了一个模型，并在第一阶段测试了混合物。