Improvement of selective laser sintering in part resolution using

使用选择性激光烧结提高零件分辨率

• 批准号: 20246032
• 负责人: NIINO Toshiki
• 金额: $ 30.04万
• 依托单位: The University of Tokyo
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (A)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/en/grant/KAKENHI-PROJECT-20246032/
• 关键词: 積層造形; Additive Manufacturing; ラピッドプロトタイピング; 粉末焼結積層造形 組織工学; 担体; 粉末焼結積層造形; 組織工学; ラピッドプロトタイビング; ラピッドマニュファクチャリング

A laser sintering apparatus equipped with an optic system that can focus its beam in a spot one third diameter as small as typical commercially available. As a result, a vertical wall of 180μm in thickness and a slit of 300μm in gap were successfully built. Relationship between the beam diameter and fineness of obtained structure is investigated. The minimum wall thickness that maintains sufficient mechanical strength was obtained as 0. 6mm. To improve the resolution of tissue engineering scaffold, plastic sacrificial filler was tested.

一种激光烧结设备，配备有一个光学系统，可以将光束聚焦在一个直径为典型市售光斑直径三分之一的光斑上。结果，成功地制作了厚度为180μm的垂直壁和间隙为300μm的狭缝。研究了光束直径与结构精细度之间的关系。获得保持足够机械强度的最小壁厚为0。六毫米为了提高组织工程支架的分辨率，对塑料牺牲填料进行了实验研究。

项目成果

Toward engineering of vascularized three-dimensional liver tissue equivalents possessing a clinically significant mass

• DOI: 10.1016/j.bej.2009.10.010
• 发表时间: 2010-02
• 期刊: Biochemical Engineering Journal
• 影响因子: 3.9
• 作者: Y. Sakai;Hongyun Huang;S. Hanada;T. Niino

積層造形・機能形状創製

增材制造/功能形状创建

• 发表时间: 2011
• 作者: K.Takano;他;新野俊樹
• 通讯作者: 新野俊樹

高親水性を有する多孔質体の粉末焼結積層造形-犠牲水溶性フィラのシランカップリング処理による親水化-

高亲水性多孔体的粉末烧结增材制造-牺牲水溶性填料的硅烷偶联处理亲水化-

• 发表时间: 2011
• 作者: M.Muraoka;S.Komatsu;浜島大輔・新野俊樹
• 通讯作者: 浜島大輔・新野俊樹

粉末焼結積層造形における供給粉末の圧粉の効果に関する研究-ポリプロピレン樹脂を利用した際に生じる影響の評価-

粉末烧结增材制造中供粉压实效果的研究-使用聚丙烯树脂时的效果评价-

• 发表时间: 2010
• 作者: 浜島大輔;新野俊樹
• 通讯作者: 新野俊樹

微細粉末焼結積層造形におけるレーザパラメータの影響についての考察

激光参数对细粉烧结增材制造影响的考虑

• 发表时间: 2009
• 作者: 長谷川洋介;笠木伸英;守田圭佑・新野俊樹
• 通讯作者: 守田圭佑・新野俊樹