Nanodomain formation due to interstitial impurities and its effecton shape memory behavior in Ti-base shape memory alloys.

间隙杂质引起的纳米域形成及其对钛基形状记忆合金形状记忆行为的影响。

• 批准号: 23860021
• 负责人: TAHARA Masaki
• 金额: $ 2.08万
• 依托单位: Tokyo Institute of Technology
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Research Activity Start-up
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/en/grant/KAKENHI-PROJECT-23860021/
• 关键词: マルテンサイト変態; 形状記憶合金; 超弾性; チタン合金

In this study, the abnormal temperature dependence of shape memory behavior was investigated from the view point of interstitial impurities by in situ x-ray diffraction measurements and in situ transmission electron microscope observation. As a result, the origin of the abnormal temperature dependence of shape memory behavior was nano-sized (about 3nm) lattice modulation structure (nanodomains) which was introduced by interstitial impurities.

本研究从间隙杂质的角度出发，通过原位X射线衍射和原位电子显微镜观察，研究了形状记忆行为与温度的反常关系。结果表明，形状记忆行为的反常温度依赖性起源于间隙杂质引入的纳米尺度(约3 nm)晶格调制结构(纳米域)。

项目成果

Ti-Nb-O合金における等温マルテンサイト変態挙動

Ti-Nb-O 合金的等温马氏体相变行为

• 发表时间: 2013
• 作者: 田原正樹;稲邑朋也;金熙榮;細田秀樹;宮崎修一
• 通讯作者: 宮崎修一

"Ti-Nb合金のα"マルテンサイトと侵入型原子の関係

Ti-Nb合金中“α”马氏体与间隙原子的关系

• 发表时间: 2012
• 作者: 田原正樹;稲邑朋也;金熙榮;細田秀樹;宮崎修一
• 通讯作者: 宮崎修一

Ti基合金の内部組織と形状記憶特性に及ぼす酸素原子の影響

氧原子对钛基合金内部结构和形状记忆性能的影响

• 发表时间: 2011
• 作者: 田原正樹;金熙榮;稲邑朋也;細田秀樹;宮崎修一
• 通讯作者: 宮崎修一

Effect of interstitial impurities on microstructure and martensitic transformation behavior of Ti-23 at.% Nb alloy

效果%20of%20间质%20杂质%20on%20显微组织%20和%20马氏体%20相变%20行为%20of%20Ti-23%20at.%%20Nb%20合金

• 发表时间: 2011
• 作者: 寺崎寛章、草間政寛;ほか;M.Tahara,H.Y.Kim,T.Inamura,H.Hosoda,S.Miyazaki
• 通讯作者: M.Tahara,H.Y.Kim,T.Inamura,H.Hosoda,S.Miyazaki

Ti-Nb-O合金における内部組織と形状記憶特性の温度依存性

Ti-Nb-O 合金内部结构和形状记忆性能的温度依赖性

• 发表时间: 2012
• 作者: 田原正樹;金熙榮;稲邑朋也;細田秀樹;宮崎修一
• 通讯作者: 宮崎修一