Development of circulation type building constructions and materials reusing construction waste.

品质改良材料(熟石灰、贝壳灰、植物油、木炭、硅藻土、海水)。粉刷工匠传下来的废纸和废纸混合在KABETSUCHI中，检查外观和强度。由于碳酸钙干燥，熟石灰和贝壳石灰的外观能够确认光泽和薄膜。因此，两者都可以预期可以减少干燥过程中的裂纹。在KABETSUCHI中，木炭和海水的混合比标准模型更强，而在其他材料情况下，这些强度下降。在KABETSUCHI中混入废纸比标准模型更具韧性，其他材料显示出与其相似的价值。然而，目前的测试方法由于测试难度大，需要测量准确的数值。用木质素制成三种不同配比的测试材料，分别由锯末、废弃纤维和纸组成。我们练习…的绩效考核更多关于VOC的释放，绝缘和吸水性，以及材料表面的水分释放。在绝缘试验的情况下，为了提高绝缘性能，制作了三种中空间距的材料。在VOC释放试验中，由于VOC释放速度较慢，认为废纸和木质素对空气的污染风险较小，抑制了VOC的释放速度。在绝缘试验中，1号材料试件的导热系数为0.044(W/MK)，其热导率为0.044(W/MK)。在以多个细孔为秸秆的情况下，中空间距试件的保温效果更好。在吸放湿测试中，具有良好绝缘性能的1号材料试件在特性曲线上显示出最大的吸湿放湿场梯度，且优于吸湿放湿性能。然而，由于材料试件1号很容易断裂，硬化剂应该使用比本试验使用的木质素更大的粘接强度。较少

The quality improvement material (slaked lime, shell lime, vegetable oil, charcoal, diatomaceous earth, sea water.) handed down by the plasterer craftsman and waste (waste paper) is mixed in KABETSUCHI, and appearance and strength were examined.The appearance of slaked lime and shell lime was able to confirm gloss and film, since calcium carbonate dries. Therefore, both can anticipate that the crack in the drying can be reduced.Charcoal and sea water are mixed in KABETSUCHI is stronger than the standard model, and in other material case, those strengths decrease. Waste paper is mixed in KABETSUCHI is more tenacious than the standard model, and other materials shows the similar value to it. However, it is necessary that the accurate value is measured in present test method, because it is difficult, examination.Three type test materials with the different compound ratio that are compounded of sawdust, disposal fiber and paper are made hard by Lignin. We practice the performance examinati … More ons about VOC release, insulation and absorbency and release of moisture from the material surface. In case of insulation test, three type materials which have hollow spacing is manufactured because of heightening the insulation performance. In the VOC release test, as the VOC release speed was low, it was thought small the air pollution risk by the disposal paper and the lignin made hold down the VOC release speed. In insulation test, the material test piece No.1 compounded the ratio of the saw, disposal giber and paper to 3-1-1 has the low thermal conductivity of 0.044 (W/mK). Test piece with hollow spacing is superior in the insulation effect at the case of the type having the multi thin hole as straw. In absorbency and release of moisture test, the material test piece No.1 having good insulation performance shows the largest gradient of absorbency and release of moisture field in the characteristic curve and is superior the absorbency and release of moisture performance. However, as the material test piece No.1 is easily broken, the hardening agent should be use the greater adhesive strength something than the lignin used this test. Less