Elucidation of Physical Properties of Novel Barium Titanate and Development of Process Technology for Application

新型钛酸钡物理性质阐明及应用工艺技术开发

• 批准号: 19360299
• 负责人: AKISHIGE Yukikuni
• 金额: $ 8.82万
• 依托单位: Shimane University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (B)
• 财政年份: 2007
• 资助国家: 日本
• 起止时间: 2007 至 2009
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-19360299/
• 关键词: 誘電体物性; セラミックス; 単結晶育成; ナノ材料; 配向制御; 鉛フリー; 強誘電体; 圧電体; チタン酸バリウム; 単結晶; 誘電率; リラクサー

On novel barium titanate (BaTi_2O_5), which is difficult to synthesize because it decomposes at high temperatures, we tried to develop process technology for application. By using sol-gel powders as a starting material and a Spark Plasma Sintering technique, dense and orientated ceramics were synthesized. Furthermore, by using MnO_2 as sintering-additives, dense ceramics were successfully synthesized without using any special sintering techniques. In KF-doped BaTi_2O_5, the Curie-temperature T_C steeply decreases with increasing content of KF, and a relaxor state appears. Single crystals with 3-5 mm in length were obtained.

对高温分解而难以合成的新型钛酸钡（BaTi_2O_5），我们尝试开发应用的工艺技术。以溶胶-凝胶粉末为原料，采用放电等离子烧结技术，制备了致密、取向的陶瓷。此外，以MnO_2为烧结助剂，在不采用任何特殊烧结工艺的情况下，成功地合成了致密的陶瓷。在KF掺杂的BaTi_2O_5中，居里温度T_C随着KF含量的增加而急剧下降，出现驰豫状态。获得了长度为3-5 mm的单晶。

项目成果

Neutron Power Diffraction Study of the Phase Transition in BaTi_2O_5

BaTi_2O_5相变的中子功率衍射研究

• 发表时间: 2007
• 期刊: Ferroelectrics 346
• 作者: H. Shigematsu;et. al.
• 通讯作者: et. al.

BaTi2O5ナノ粒子を用いたセラミックスの合成と物性

BaTi2O5纳米颗粒陶瓷的合成及物理性能

• 发表时间: 2007
• 作者: 秋重幸邦;徐軍
• 通讯作者: 徐軍

チタン酸バリウム系蛍光物質

钛酸钡荧光材料

• 发表时间: 2009

BaTi2O5系強誘電性セラミックス製造方法

BaTi2O5基铁电陶瓷的制造方法

• 发表时间: 2009

BaTi2O5セラミックスの作製と誘電特性

BaTi2O5陶瓷的制备及其介电性能

• 发表时间: 2009
• 作者: 本多一雄;塚田真也;秋重幸邦
• 通讯作者: 秋重幸邦